Reaction condition optimization and kinetic investigation of roasting zinc oxide ore using (NH<Subscript>4</Subscript>)<Subscript>2</Subscript>SO<Subscript>4</Subscript>

An orthogonal test was used to optimize the reaction conditions of roasting zinc oxide ore using (NH₄)₂SO₄. The optimized reaction conditions are defined as an (NH₄)₂SO₄/zinc molar ratio of 1.4:1, a roasting temperature of 440°C, and a thermostatic time of 60 min. The molar ratio of (NH₄)₂SO₄/zinc is the most predominant factor and the roasting temperature is the second significant factor that governs the zinc extraction. Thermogravimetric–differential thermal analysis was used for (NH₄)₂SO₄ and zinc mixed in a molar ratio of 1.4:1 at the heating rates of 5, 10, 15, and 20 K·min-1. Two strong endothermic peaks indicate that the complex chemical reactions occur at approximately 290°C and 400°C. XRD analysis was employed to examine the transformations of mineral phases during roasting process. Kinetic parameters, including reaction apparent activation energy, reaction order, and frequency factor, were calculated by the Doyle–Ozawa and Kissinger methods. Corresponding to the two endothermic peaks, the kinetic equations were obtained.     

3,4-dichlorotoluene ammoxidation to 3,4-dichlorobenzonitrile over VPO/SiO<Subscript>2</Subscript> catalyst

Ammoxidation of 3,4-dichlorotoluene (DCT) to prepare 3,4-dichlorobenzonitrile (DCBN) over silica supported vanadium phosphorus oxide catalysts has been studied. On the VPO/SiO₂ catalyst, the influence of the reaction temperature, the molar ratio of air/DCT, the molar ratio of NH₃/DCT in the feed gas and the space velocity (v ₁) on the conversion, yield and selectivity was observed. The most appropriate reaction condition is: reactionT=673 K,n(DCT):n(NH₃):n(air)=1:7:30 andv ₁=250 h⁻¹. At this optimum reaction condition, the conversion of DCT is 97.8%; the molar yield of DCBN is 67.4%. It was found that the addition of element phosphorus can improve the yield of DCBN compared with VO/SiO₂ catalyst. Foundation item: Supported by Youth Chen-Guang Project of the Committee of Science and Technology of Wuhan (20015005042) Biography: Huang Chi(1972-), male, Ph D, Lecture, research direction: ammoxidation.     

Activity coefficients of NiO and CoO in CaO-Al2O3-SiO2 slag and their application to the recycling of Ni-Co-Fe-based end-of-life superalloys via remelting

To design optimal pyrometallurgical processes for nickel and cobalt recycling, and more particularly for the end-of-life process of Ni-Co-Fe-based end-of-life (EoL) superalloys, knowledge of their activity coefficients in slags is essential. In this study, the activity coefficients of NiO and CoO in CaO-Al₂O₃-SiO₂ slag, a candidate slag used for the EoL superalloy remelting process, were measured using gas/slag/metal equilibrium experiments. These activity coefficients were then used to consider the recycling efficiency of nickel and cobalt by remelting EoL superalloys using CaO-Al₂O₃-SiO₂ slag. The activity coefficients of NiO and CoO in CaO-Al₂O₃-SiO₂ slag both show a positive deviation from Raoult's law, with values that vary from 1 to 5 depending on the change in basicity. The activity coefficients of NiO and CoO peak in the slag with a composition near B=(%CaO)/(%SiO₂)=1, where B is the basicity. We observed that controlling the slag composition at approximately B=1 effectively reduces the cobalt and nickel oxidation losses and promotes the oxidation removal of iron during the remelting process of EoL superalloys.     

Gracefulness of several unconnected graphs with wheel

In the paper, we study the gracefulness of several unconnected graphs related to wheel. For natural number p ≥1,t ≥1, let n =2t +3, 2t +4, which proved W_n∪K_(p,t)~(1)∪K_(p,t)~(2) is graceful; for p ≥1, t ≥1,let n=2t+3,2t+4, then W_(n,2n+1)∪K_(p,t)~(1)∪K_(p,t)~(2) is graceful and for m≥1,r ≥1, let n =2m +5, W_(n,2n+1) ∪( C_3∨K m) U St( r)is graceful.     

不同钙化剂对高钒渣酸浸提钒的影响

针对传统钒渣钠化焙烧-水浸提钒工艺的不足,确定对钒渣钙化焙烧-酸浸提钒进行研究。在理论分析的基础上,本研究以高钒渣为原料,研究了钙化焙烧-酸浸提钒过程中3种钙化剂(CaSO4、CaCO3、CaO)的焙烧机理以及对提钒效果的影响。研究结果表明:钒浸出率随焙烧温度的升高先增大后减小,且在1 450K时达到最大值;钙化剂配比为100%CaSO4时提钒率最大;在目前实验室研究条件下,钒的浸出率最大可达93.53%。     

A novel hydrothermal method for zinc extraction and separation from zinc ferrite and electric arc furnace dust

A novel hydrothermal process was developed to extract zinc from pure zinc ferrite (ZnFe₂O₄) nanopowder and zinc-containing electric arc furnace (EAF) dust using hexahydrated ferric chloride (FeCl₃·6H₂O) as a decomposing agent. The effects of solid FeCl₃·6H₂O to ZnFe₂O₄ ratio by mass (R_F/Z), hydrothermal reaction temperature, and time on zinc extraction were systematically investigated. In the results, when the hydrothermal reaction is conducted at 150℃ for 2 h with R_F/Z of 15:20, the efficiency of zinc extraction from ZnFe₂O₄ reaches 97.2%, and the concentration of ferric ions (Fe3+) in the leaching solution is nearly zero, indicating a high selectivity for zinc. In addition, the zinc extraction efficiency from the EAF dust reaches 94.5% in the case of the hydrothermal reaction performed at 200℃ for 10 h with the solid FeCl₃·6H₂O to EAF dust ratio by mass (R_{F/EAF dust}) of 15:10. Zinc and iron separation is achieved by adjusting the pH value of the leaching solution according to the different precipitation pH values of metal hydroxides.     

Binding number,minimum degree and bipancyclism in bipartite graphs

Let G =(V_1,V_2,E) be a balanced bipartite graph with2 n vertices.The bipartite binding number of G,denoted by B(G),is defined to be n if G =K_n and min i∈{1,2}|N(S)|n min |N(S)|/|S|otherwise.We call G bipancyclic if it contains a cycle of every even length m for 4 ≤ m ≤ 2n.A theorem showed that if G is a balanced bipartite graph with 2n vertices,B(G) 3 / 2 and n 139,then G is bipancyclic.This paper generalizes the conclusion as follows:Let 0 c 3 / 2 and G be a 2-colmected balanced bipartite graph with 2n(n is large enough) vertices such that B(G) c and δ(G)(2-c)n/(3-c)+2/3.Then G is bipancyclic.     

Effect of SiO<Subscript>2</Subscript> addition on the microstructure and electrical properties of ZnO-based varistors

The microstructure and electrical properties of ZnO-based varistors with the SiO₂ content in the range of 0–1.00mol% were prepared by a solid reaction route. The varistors were characterized by scanning electron microscopy, X-ray diffraction, energy-dispersive X-ray spectrometry, inductively coupled plasma-atomic emission spectrometry, and X-ray photoelectron spectroscopy. The results indicate that the average grain size of ZnO decreases with the SiO₂ content increasing. A new second phase (Zn₂SiO₄) and a glass phase (Bi₂SiO₅) are found. Element Si mainly exists in the grain boundary and plays an important role in controlling the Bi₂O₃ vaporization. The electric measurement shows that the incorporation of SiO₂ can significantly improve the nonlinear properties of ZnO-based varistors, and the nonlinear coefficients of the varistors with SiO₂ are in the range of 36.8–69.5. The varistor voltage reaches the maximum value of 463 V/mm and the leakage current reaches the minimum value of 0.11 μA at the SiO₂ content of 0.75mol%.     

A generalized funk’s section theorem for measures

If L is a star body in R~n whose central(n-i)-slices have the same(n-i)-dimensional measure μ_(n-i)(with appropriate density)as the central(n-i)-slices of an origin-symmetric star body K,then the corresponding n-dimensional measures μ_n of K and L satisfy μ_n(K)≤μ_n(L).This extends a generalized Funk’s section theorem for volumes to that for measures.     

Nonclassical crystallization of zinc carbonate hydroxide hydrate nanofilm mediated by calcium ions

To satisfy the demand of zinc oxide (ZnO) with advanced muti-functional properties, significant efforts have been made in synthesizing ZnO with various structure and morphology. In particular, hydrothermal method has attracted considerable attentions, in which Zn₄CO₃(OH)₆·H₂O (ZCHH) is commonly found as a metastable precursor. However, the formation and crystallization mechanisms of ZCHH are still lacking and urgently needed. In the present study, the crystallization pathway of ZCHH was systematically investigated, and the results demonstrate that the amorphous zinc carbonate (AZC) was an even more unstable precursor. AZC nanoparticles typically aggregated to form one-dimensional (1D) ZCHH nanorods, however, two-dimensional (2D) ZCHH nanofilms were obtained in the presence of a certain concentration of calcium ion. The results suggest that calcium ions could promote the partial dissolution of AZC and facilitate the aggregation of AZC nanoparticles to form crystalline nanofilm. Moreover, 2D ZnO nanofilms could be obtained by heat treatment of the ZCHH nanofilms. The calcium ion mediated nonclassical crystallization pathway provides inspiration for fabrication of ZnO with controlled morphology and offers new opportunities for inorganic regulated material synthesis.     

Lüroth Expansion Digits and Maclaurin's Inequality

It is well known that for almost all real number x, the geometric mean of the first n digits d_i(x) in the Lüroth expansion of x converges to a number K_0 as n→∞. On the other hand, for almost all x, the arithmetric mean of the first n Lüroth expansion digits d_i(x) approaches infinity as n→∞. There is a sequence of refinements of the AM-GM inequality, Maclaurin's inequalities, relating the 1/k-th powers of the k-th elementary symmetric means of n numbers for 1≤k≤n. In this paper, we investigate what happens to the means of Lüroth expansion digits in the limit as one moves f(n) steps away from either extreme. We prove sufficient conditions on f(n) to ensure divergence when one moves away from the arithmetic mean and convergence when one moves f(n) steps away from geometric mean.     

钼精矿焙烧处理过程中典型杂质元素的热力学行为及分析

通过模拟实验结合X射线荧光光谱仪(X-ray fluorescence spectrometer,XRF)、电感耦合等离子光谱发生仪(inductively coupled plasma spectrometer,ICP)及矿物解离分析仪(mineral liberation analyser,MLA)等研究了钼精矿焙烧处理流程中多种杂质元素间的相互作用,在MLA对物相定量分析的基础上,采用Factsage7.0软件分析了钼精矿焙烧过程中不同杂质元素反应进行的热力学条件。结果表明：杂质元素在钼精矿及后续处理流程中的分布存在明显的粒度偏析,主要表现为K、Si等杂质更多以大分子量的矿物形式赋存在较粗粒度的钼精矿中,而Fe、Ca、Cu等杂质则更多以FeS₂、CaSO₄、CuFeS₂等小分子量的化合物形式赋存在较细粒度的钼精矿中。FeS₂、CaSO₄和SiO₂等杂质会在高温焙烧过程中与MoO₃形成致密度较高的混合物,降低Mo的浸出率。云母在钼...     

Alkaline digestion behavior and alumina extraction from sodium aluminosilicate generated in pyrometallurgical process

In pyrometallurgical process, Al-and Si-bearing minerals in iron and aluminum ores are easily transformed into sodium aluminosilicates in the presence of Na₂O constituents, which alters the leaching behaviors of Al₂O₃ and SiO₂. It was confirmed that sodium aluminosilicates with different phase compositions synthesized at various roasting conditions were effectively digested in the alkaline digestion process. Under the optimum conditions at temperature of 100-120℃, liquid-to-solid ratio (L/S) of 10:2 mL/g, caustic ratio of 4, and Na₂O concentration of 240 g/L, the actual and relative digestion ratio of Al₂O₃ from the synthesized sodium aluminosilicates reached maximums of about 65% and 95%, respectively, while SiO₂ was barely leached out. To validate the superior digestion property of sodium aluminosilicate generated via an actual process, the Bayer digestion of an Al₂O₃-rich material derived from reductive roasting of bauxite and comprising Na_1.75Al_1.75Si_0.25O₄ was conducted; the relative digestion ratio of Al₂O₃ attained 90% at 200℃.     

Multi-index analysis of the melting process of laterite metallized pellet

Herein, a multi-index analysis of the nickel content of an alloy, output rate of the alloy, nickel recovery rate, and iron recovery rate during the melting of laterite metallized pellets was performed. The thermodynamic reduction behavior of oxides such as NiO, FeO, Fe₃O₄, and Cr₂O₃ was studied using the FactSage software, which revealed that SiO₂ is not conducive to the reduction of iron oxides, whereas the addition of basic oxides such as CaO and MgO is beneficial for the reduction of iron oxides. On the basis of a comprehensive analysis to achieve greater nickel recovery and lower iron recovery rates, the optimum experimental parameters in the orthogonal experiment were A3B1C3 (t=30 min, C/O=0.4, R=1.2); the indicators w_Ni, φ_alloy, η_Ni, and η_Fe had values of 15.0wt%, 12.1%, 44.9%, and 96.4%, respectively. In single-factor experiments, increasing basicity (R) substantially improved the separation effect in the low-basicity range 0.5 ≤ R ≤ 0.8 but not in the high-basicity range 0.8 ≤ R ≤ 1.2. Similar results were obtained for the effect of the C/O ratio. Moreover, the recovery rate of nickel increased with increasing recovery rate of iron.     

Synthesis of glass ceramics from kaolin and dolomite mixture

Cordierite-and anorthite-based binary glass ceramics of the CaO-MgO-Al₂O₃-SiO₂ (CMAS) system were synthesized by mixing local and abundant raw minerals (kaolin and doloma by mass ratio of 82/18). A kinetics study reveals that the activation energy of crystallization (Ea) calculated by the methods of Kissinger and Marotta are 438 kJ·mol-1 and 459 kJ·mol-1, respectively. The Avrami parameter (n) is estimated to be approximately equal to 1, corresponding to the surface crystallization mechanism. X-ray diffraction (XRD) analysis shows that the anorthite and cordierite crystals are precipitated from the parent glass as major phases. Anorthite crystals first form at 850℃, whereas the μ-cordierite phase appears after heat treatment at 950℃. Thereafter, the cordierite allotropically transforms to α-cordierite at 1000℃. Complete densification is achieved at 950℃; however, the density slightly decreases at higher temperatures, reaching a stable value of 2.63 kg·m-3 between 1000℃ and 1100℃. The highest Vickers hardness of 6 GPa is also obtained at 950℃. However, a substantial decrease in hardness is recorded at 1000℃; at higher sintering temperatures, it slightly increases with increasing temperature as the α-cordierite crystallizes.     

Fault-tolerant cycles embedding in folded hypercubes

The generalized conditional fault-tolerant embedding is investigated, in which the n-dimensional folded hypercube networks(denoted by FQ_n) acts as the host graph, and the longest fault-free cycle represents the guest graph. Under the conditions looser than that of previous works, it is shown that FQ_n has a cycle with length at least 2~n-2︱F_v︱ when the number of faulty vertices and non-critical edges is at most 2n-4; where ︱F_v︱ is the number of faulty vertices. It provides further theoretical evidence for the fact that FQ_n has excellent node-fault-tolerance and edge-fault-tolerance when used as a topology of large scale computer networks.     

Vertex disjoint cycles in intersection graphs of bases of matroids

The intersection graph of bases of a matroid M=(E, B) is a graph G=G~I(M) with vertex set V(G) and edge set E(G) such that V(G)=B(M) and E(G)={BB′:|B∩B′|≠0, B, B′∈B(M), where the same notation is used for the vertices of G and the bases of M. Suppose that|V(G~I(M))| =n and k_1+k_2+…+k_p=n, where k_i is an integer, i=1, 2,…, p. In this paper, we prove that there is a partition of V(G~I(M)) into p parts V_1 , V_2,…, V_p such that |V_i| =k_i and the subgraph H_i induced by V_i contains a k_i-cycle when k_i ≥3, H_i is isomorphic to K_2 when k_i =2 and H_i is a single point when k_i =1.     

硅铝摩尔比对MCM-22的酸性及苯与丙烯烷基化催化性能的影响

以六亚甲基亚胺为模板剂,通过动态水热晶化法合成硅铝摩尔比为20～60的分子筛,采用XRD表征其物相结构;并采用NH₃-TPD,吡啶吸附等方法表征其酸性质;利用气-液固反应和液-固反应,比较不同硅铝摩尔比的MCM-22分子筛在苯与丙烯烷基化反应的催化性能。结果表明:当硅铝摩尔比在30～60时,可以合成出比较纯的MCM-22分子筛,且随着硅铝摩尔比的增加,分子筛的B酸量逐渐增加,所表现出的烷基化活性也随之增加。当硅铝摩尔比为40时,目标产物异丙苯的选择性达最高值,副产物二异丙苯和三异丙苯的摩尔分数最低,但正丙苯的摩尔分数却最高,这与催化剂中B酸量及其所占比例有关。     

Phase modification and dielectric properties of a cullet-paper ash-kaolin clay-based ceramic

Novel ceramics from waste material made of (x) paper ash-(80-x) cullet-20 kaolin clay (10wt% ≤ x ≤ 30wt%) were successfully synthesized using a conventional solid-state reaction technique. Energy-dispersive X-ray analysis confirmed the presence of Si, Ca, Al, and Fe in the waste material for preparing these ceramics. The influence of the cullet content on the phase structures and the dielectric properties of these ceramics were systematically investigated. The impedance spectra were verified in the range from 1 Hz to 10 MHz at room temperature. The phase of the ceramics was found to primarily consist of wollastonite (CaSiO₃), along with minor phases of γ-dicalcium silicate (Ca₂SiO₄) and quartz (SiO₂). The sample with a cullet content of 55wt% possessed the optimum wollastonite structure and exhibited good dielectric properties. An increase of the cullet content beyond 55wt% resulted in a structural change from wollastonite to dicalcium silicate, a decrease in dielectric constant, and an increase in dielectric loss. All experimental results suggested that these novel ceramics from waste are applicable for electronic devices.>     

Boron separation from Si-Sn alloy by slag treatment

This study investigates a purification process for metallurgical-grade silicon (MG-Si) in which Si is alloyed with tin (Sn) and CaO-SiO₂-CaCl₂ slag is used to remove boron (B) impurity. Acid leaching was performed to remove the Sn phase after slag refining to recover high-purity Si from the Si-Sn alloy. The effect of refining time was investigated, and acceptable refining results were realized within 15 min. The effects of slag composition and Sn content on the removal of B were also studied. The results indicate that increasing Sn content favors B removal. With the increase of Sn to 50% of the alloy, the final B content decreased to 1.1×10-4wt%, 93.9% removal efficiency.