25Si2Mn2CrNiMoV钢的疲劳性能研究

本文通过对25Si 2Mn2CrNiMoV钢疲劳性能的研究,对它的疲劳裂纹扩展特性和疲劳断裂机制进行了分析,还讨论了疲劳断口和组织之间的关系.试验结果证明:本钢种的疲劳强度σ_(-1)很高,其值高于70kg/mm~2.在200～300℃回火时疲劳裂纹的扩展抗力也很高,此回火温度范围适为钢的最佳强轫配合的回火温度范围.钢中含有2%Si,使回火马氏体脆性出现的温度区间明显推迟.为静强度和疲劳性能同时达到较高的水平创造了条件.     

钢的疲劳裂纹萌生与扩展的电子显微断口分析

本文采用电子显微断口分析方法,对20SiMn2MoV低碳马氏体钢,45Cr和T12钢淬火不同回火态和34CrNi3Mo电站大锻件用铜的疲劳裂纹萌生与扩展机制进行了研究.并着重在材料的不同强塑配合引起断裂机制变化的关系中做了探讨;总结了三个区之间机制转变的条件;给出了较初步的疲劳断裂机制图;从材料强度方面提出了各阶段的主要控制因素,从而为改善材料疲劳抗力提供了一些依据.     

GCr15钢的疲劳和断裂

本文研究了热处理对GCr15轴承钢断裂韧性K_(Ic)和疲劳裂纹扩展速率da/dN的影响。试验结果表明:基体成分及组织是影响K_(Ic)和da/dN的主要因素;淬火加热温度升高,K_(Ic)降低,da/dN增快;提高回火温度,K_(Ic)增加,da/dN减慢,但在230℃回火时,因处于回火马氏体脆性区,K_(Ic)急烈下降,da/dN增加;在低温回火范围内,淬火加热温度对K_(Ic)和da/dN的影响远比回火温度对这两种力学性能指标的影响强烈。对GCr15钢疲劳断口和疲劳裂纹扩展过程观察后认为:在门槛区附近,疲劳裂纹的扩展以沿晶为主;中速区则以断续的再生核机制进行扩展;快速区至最后断裂阶段表现为准解理和沿晶断。     

B对冷轧IF钢板疲劳性能的影响

对比研究了Ｂ对Ｔｉ添加和Ｔｉ,Ｎｂ复合添加的冷轧ＩＦ钢板的显微组织和疲劳性能的影响·研究结果表明 ,Ｂ可以细化这两种ＩＦ钢的退火组织 ,改善晶界结合强度 ,提高疲劳强度·疲劳断口分析结果表明 ,ＩＦ钢表现为沿晶断裂特征 ,Ｂ可使ＩＦ钢断裂特征得以改善 ,由沿晶断裂转变成穿晶断裂·B对冷轧IF钢板疲劳性能的影响@刘常升 @才庆魁 @金成柱     

B对冷轧IF钢板焊接疲劳性能的影响

对比研究了B对Ti添加和Ti、Nb复合添加的冷轧IF钢板经电阻焊接前后的显微组织和疲劳性能的影响·结果表明,B可以细化这两种IF钢的退火组织和焊接热影响区组织,改善晶界结合强度,提高焊接疲劳强度·疲劳断口分析结果表明,IF钢焊后表现为沿晶断裂特征,B可使IF钢断裂特征得以改善,由沿晶断裂转变成穿晶断裂     

低碳马氏体型超高强度钢的组织结构和疲劳断裂行为

本文在低碳马氏体型超高强度钢强韧性规律研究的基础上,系统地研究了疲劳断裂规律。试验结果表明,典型钢种25Si2Mn2CrNiMoV通过950℃加热油淬350℃回火,其疲劳强度(σ_(-1),σ_(-1N)等)和裂纹扩展抗力(dα/dN,ΔK_(th)等)可以实现最优化。通过对疲劳裂纹的原位透射电子显微分析,发现了疲劳裂纹尖端塑性区内板条马氏体晶体交界处的残余奥氏体薄膜发生应变诱发马氏体相变,观察到疲劳裂纹扩展过程中组织结构的变化情况,从而讨论了显微组织结构与疲劳断裂行为的对应关系。     

回火温度对40Cr钢疲劳损伤特性的影响

研究了不同回火温度下40Cr钢的高周疲劳损伤特性.通过损伤量的变化测量和扫描电镜下损伤不同阶段微观组织的观察,分析回火温度对疲劳损伤特性的影响.实验结果表明,结构钢材料在高周疲劳载荷作用下,疲劳损伤过程分为3个阶段,即微孔洞萌生区、微裂纹萌生区、宏观裂纹萌生区.疲劳裂纹的萌生期随着回火温度的升高而增加,在本实验的载荷作用下,高温回火的40Cr钢的裂纹萌生期在3万周以上,中温回火的裂纹萌生在2.8万周,而低温回火的裂纹萌生期在2万周.     

深冷处理对EA4T车轴钢马氏体组织及短裂纹行为的影响

利用光学显微镜(OM)、维氏硬度计、X射线衍射(XRD)和电子背散射衍射(EBSD)技术等,开展深冷处理与回火顺序对EA4T车轴钢马氏体组织及其疲劳断裂性能影响的研究。研究结果表明：无论是“回火+深冷”处理还是“深冷+回火”处理,均能有效细化材料的微观组织,从而提高硬度和位错密度,但组织中含量较少的残余奥氏体无法通过深冷处理继续向马氏体转化;相对而言,经“深冷+回火”处理的试样晶粒尺寸细化效果最佳,且小角度晶界占比最多,可有效抑制裂纹的萌生;经“深冷+回火”处理后,材料微观组织对裂纹扩展的阻碍作用最强,裂纹扩展速率的下降更明显,疲劳断裂性能相对更优。     

XCQ16和20Mn2车轴用钢疲劳失效的微观机理

利用扫描电镜(SEM)对XCQ16和20Mn2两种车轴用钢疲劳断口和裂纹扩展断口进行分析,研究疲劳失效过程中的裂纹萌生及扩展机理.结果表明:裂纹均是从试样表面萌生,非金属夹杂和位错是主要的萌生机制;XCQ16钢在疲劳断口中部区的裂纹闭合效应大于20Mn2钢,裂纹扩展较慢;两者在裂纹扩展区的扩展机理不同,XCQ16钢属于塑性断裂,20Mn2钢属于解理断裂;在非金属夹杂上,XCQ16钢多含氧化物和硫化物的混合夹杂,20Mn2钢主要是氧化物夹杂,混合夹杂对材料的疲劳性能影响较小.     

几种结构钢经不同热处理后的低温断裂韧性

本文研究了机械工程常用的几种结构钢经不同热处理后在常温和低温下的断裂韧性K_(IC)或K_(IR),以及这些材料在不同温度下的断裂机制。结果表明,45Cr钢淬火550℃回火后,常温和低温K_(IC)值较20Cr钢淬火200℃回火的高,但45Cr钢淬火390℃回火后的断裂韧性不如20Cr钢淬火200℃回火的。20Cr钢经临界区处理后,低温断裂韧性优于普通淬火的。42CrMo钢从过热温度淬火后,断裂韧性差。断裂机制和K_(IC)值都随试验温度而变化。奥氏体晶粒大小和马氏体板条束尺寸显著影响低温断裂韧性,临界区淬火后马氏体板条束尺寸较小,因而低温断裂韧性高。     

残铝在35CrNi3MoV钢中的作用

研究了残铝在３５ＣｒＮｉ３ＭｏＶ钢中的作用与作用机理。结果表明，３５ＣｒＮｉ３ＭｏＶ钢的最佳残铝含量为０．０１０％Ａｌ。     

43CrNi2MoVA钢的Bauschinger效应与强化模型

应用自编程序在MTS试验机上对43CrNi_2MoVA钢的Bauschinger效应进行了测定,探讨了应变水平、应变历史对Bauschinger效应系数(BEF)的影响,并对该材料的强化模型进行了分析研究。     

Enhanced fatigue property by fabricating a gradient nanostructured surface layer in a reduced-activation steel

Reduced activation ferritic/martensitic (RAFM) steels have been selected as candidate structural materials for future advanced nuclear power systems. In the present work, the influence of a gradient nanograined surface layer on the fatigue properties of RAFM steels was studied. A gradient nanostructured (GNS) surface layer with a thickness of ～85 ?μm was prepared on RAFM steel utilizing surface mechanical rolling treatment (SMRT). The mean grain size was approximate 43 ?nm at the topmost surface and increased gradually with depth. The results of the stress-controlled tension-compression fatigue experiments showed that the fatigue life enhanced approximately 6 times in the SMRT samples compared to the corresponding base metal counterparts. The relationship between the applied stress amplitude and the fatigue lifetime, and the fracture morphology showed that the surface strengthening and strain delocalization were caused by GNS, which suppressed surface crack initiation process, and hence the fatigue properties of RAFM steels improved. In addition, the deformation compatibility in GNS and coarse-grained boundaries leading to more dislocation interactions and accumulation during the cyclic process, also plays a crucial role in enhancing the fatigue properties of RAFM steel.     

25Cr2MoV离子渗氮齿轮疲劳强度的试验

本文对２５Ｃｒ２ＭｏＶ离子渗氮齿轮所进行的齿面接触疲劳和轮齿弯曲疲劳试验研究，得出了这种齿轮疲劳寿命分布规律和疲劳强度分布规律的结论，并求得这种齿轮的Ｒ－Ｓ－Ｎ线簇方程以及各种可靠度下的齿轮接触疲劳极限应力值和轮齿弯曲疲劳极限应力值。     

304不锈钢超高周疲劳试验裂尖马氏体相变

采用超声疲劳试验技术对304不锈钢进行了超高周疲劳试验,并用扫描电镜对疲劳断口进行了分析。结果显示304不锈钢在Nf=8.60×108,σα=±206MPa的疲劳断口SEM形貌中的第一裂纹扩展区高倍放大像出现羽毛状片层结构,通过X射线衍射发现在奥氏体峰旁有铁素体峰出现。通过分析推测,304不锈钢超高周疲劳试验形变诱发马氏体相变。     

12Cr1MoV钢小直径管焊接接头取消焊后热处理的组织研究

本文研究了12Cr1MoV钢小直径管焊接接头在焊后进行热处理和不进行热处理时的高温时效特性和组织，结果表明，焊后热处理对高温长期运行的接头组织是不利的。     

表面强化处理钢的疲劳断裂韧性

本文首次把疲劳断裂韧性概念引入到表面化学热处理强化钢中。试验结果表明:在较低过载应力下存在内部疲劳裂纹时,“鱼眼”半径可定义为临界裂纹半长;对每一处理状态,疲劳断裂韧性可视为一定值;除强度和塑性外,表面化学热处理钢中所特有的残余应力对疲劳断裂韧性也具有重要的影响;在碳氮共渗层中,当裂纹向着高碳含量方向扩展时,残余压应力对裂纹的扩展起着显著的抑制作用。     

Qualitative and quantitative characterizati ons of fracture surfaces of AL6XN super-austen itic stainless steel fatigued at different stress amplitudes

Fracture surface features of the AL6XN super-austenitic stainless steel fatigued at different stress amplitudes were observed by SEM and quantitatively analyzed by a fractal method.It was found that th...     

12Cr1MoV连铸钢坯高温力学性能研究

在Gleeble-1500热模拟机上进行了低合金钢12Cr1MoV热模拟实验,测试了从600℃到峰值温度,涵盖了连铸时从结晶器到输出辊道的整个温度范围,得出了12Cr1MoV在不同应变速率不同温度下的流变曲线、强度曲线和热塑性曲线,观察了不同温度下试样的断口形貌组织.实验结果表明:低合金钢12Cr1MoV的ZST为1425℃,ZDT为1400℃.在1100~1300℃范围内,钢的断面收缩率均大于60%,具有良好的塑性;脆性范围为1350℃到熔点和900℃以下.     

Test Research on Reliability of Gear-tooth Bending Fatique Strength for Through Hardening Steel 37SiMn2MoV

论述３７ＳｉＭｎ２ＭｏＶ调质齿轮轮齿弯曲疲劳强度的可靠性试验研究,该试验是在英国制造的ＥＭＲ－１６０３型电磁谐振疲劳试验机上进行的,分４个应力级,每个应力级的试验样本不少于６个。在试验数据基础上,拟合出Ｒ－Ｓ－Ｎ曲线及方程,最后求得不同可靠度下３７ＳｉＭｎ２ＭｏＶ调质齿轮轮齿的弯曲疲劳强度极限。