C—Si—Mn系热轧双相钢显微组织与力学性能之间的关系

通过对热轧试样的组织性能测试,研究了热轧双相钢显微组织与力学性能之间的关系。研究发现,铁素体和马氏体强度是影响力学性能的主要因素。建立了C-Si-Mn系热轧双相钢力学性能的数学模型,可以作为热轧双相钢基本力学性能参数预测的理论依据。     

Effects of overaging temperature on the microstructure and properties of 600 MPa cold-rolled dual-phase steel

C–Mn steels prepared by annealing at 800°C for 120 s and overaging at 250–400°C were subjected to pre-straining (2%) and baking treatments (170°C for 20 min) to measure their bake-hardening (BH2) values. The effects of overaging temperature on the microstructure, mechanical properties, and BH2 behavior of 600 MPa cold-rolled dual-phase (DP) steel were investigated by optical microscopy, scanning electron microscopy, and tensile tests. The results indicated that the martensite morphology exhibited less variation when the DP steel was overaged at 250–350°C. However, when the DP steel was overaged at 400°C, numerous non-martensite and carbide particles formed and yield-point elongation was observed in the tensile curve. When the overaging temperature was increased from 250 to 400°C, the yield strength increased from 272 to 317 MPa, the tensile strength decreased from 643 to 574 MPa, and the elongation increased from 27.8% to 30.6%. Furthermore, with an increase in overaging temperature from 250 to 400°C, the BH2 value initially increases and then decreases. The maximum BH2 value of 83 MPa was observed for the specimen overaged at 350°C.     

热浸镀锌钢板镀层织构与耐蚀性

用X射线衍射和动电位扫描方法研究了热浸镀锌钢板镀层织构、相分布和耐蚀性的关系.实验结果表明,镀锌层中纯锌相的主要织构组分为{0002}基面织构,当镀锌层厚度增加时,纯锌相中{0002}基面织构密度水平增加,纯锌相自腐蚀电位升高、腐蚀电流密度减小以及耐蚀性增加.X射线衍射分析电化学剥离后的铁锌相,结果表明,镀锌层由纯锌相和合金相组成;电化学实验表明,镀锌层各相耐蚀性不同,合金相的耐蚀性高于纯锌相的耐蚀性,且Fe--Zn合金相的耐蚀性随铁含量的增加而增加.     

一种超高强度钢组织性能的研究

通过力学测试、金相、扫描电镜观察等方法研究了不同淬火温度下一种淬火 低温回火超高强度钢的组织性能,系统的探讨了未溶相与淬火温度的关系。结果表明：钢采用低于950℃的淬火温度,组织中存在大量未溶碳化物,当温度高于1010℃时,未溶碳化物基本溶解,马氏体板条束明显粗化,对钢的力学性能有害,适宜的淬火温度为1010℃。     

退火温度对430不锈钢冷轧板组织和力学性能的影响

针对现场生产的430不锈钢冷轧板,通过高温连续退火实验研究了退火温度对材料显微组织、强度、塑性以及各向异性性能的影响.通过实验得到了合理的两段式加热连续退火工艺:选取中间温度为600℃,加热II段的加热速率为2.3℃·s-1,最高加热温度为840℃.随着退火温度的升高,薄板的屈服强度和硬度呈明显的两阶段降低趋势,延伸率呈"S"型趋势增加,平均塑性应变比基本保持不变(1.25左右),而轧制平面各向异性指数有一定的降低.针对430不锈钢冷轧板分别建立了屈服强度与退火软化率和延伸率之间的定量关系.     

热浸Zn-Al合金镀层的助镀工艺和显微组织特征

简述了热浸Zn-Al合金镀层的助镀工艺和性能评价指标特点,论述了钢材热浸镀Zn-Al合金镀层的组成及形成过程,分析了钢中Si、Mn、P等常存元素对Zn-Al合金镀层中金属间化合物形成的影响,指出了热浸Zn-Al系多元合金镀层今后的研究方向。     

热处理工艺对40CrNiMoA合金组织及力学性能的影响

为了提高矿用链轮耐磨性,延长其使用寿命,选取电渣离心铸造40CrNiMoA合金链轮件作为母材,研究热处理工艺对40CrNiMoA合金组织和力学性能的影响。采用正交试验法,研究不同热处理工艺对合金显微硬度、摩擦磨损及拉伸强度等力学性能的影响,并将测试结果进行极差分析和综合加权评分计算,得出最优热处理工艺参数,最后进行试验验证。结果表明,正交试验法得到的最优热处理工艺为880℃淬火0.5 h, 600℃高温回火2 h,样品热处理后的组织主要为回火索氏体,维氏硬度为364 HV,抗拉强度为1 166 MPa,磨损率为0.427×10^-4 mm³/(N·m);验证试验结果与正交试验分析结果相近,且热处理后的样品性能可达到使用要求。研究结果可为矿用链轮件热处理工艺提供理论依据,对有效解决链轮耐磨性和使用寿命问题具有参考价值。     

预处理组织对低碳钢IQ&P工艺下组织及性能影响

采用γ单相区和γ+α双相区轧制并淬火工艺以及双相区再加热-淬火-碳配分( IQ&P)工艺,研究预处理组织对低碳钢室温状态多相组织特征及力学性能的影响规律. 实验用低碳钢经两种工艺轧制并淬火处理,获得马氏体和马氏体+铁素体的预处理组织,再经双相区IQ&P工艺处理后均获得多相组织. 马氏体预处理钢的室温组织由板条状亚温铁素体、块状回火马氏体以及一定比例的针状未回火马氏体和8. 2%的针状残余奥氏体组成;马氏体+铁素体预处理钢由板条状亚温铁素体、块状和针状未回火马氏体以及14. 3%的短针状或块状残余奥氏体组成. 在相同的双相区IQ&P工艺参数下,预处理组织为马氏体的钢抗拉强度为770 MPa,伸长率为28%,其强塑积为21560 MPa·%;而预处理组织为马氏体+铁素体的钢抗拉强度为834 MPa,伸长率增大到36. 2%,强塑积达到30190 MPa·%,获得强度与塑性的优良结合.     

纤维双相钢的组织形成及对性能的影响

研究了纤维双相15Mn2Nb钢组织的形成及对性能的影响.结果表明,纤维双相钢具有优异的强塑性匹配,是一种天然的复合材料.其纤维组织的获取主要取决于合金化和热处理工艺规程,而合金元素Nb阻碍铁素体再结晶是形成纤维组织的关键.     

热镀锌钢卷力学性能GBDT预报模型

针对热镀锌钢卷力学性能预报建模条件属性选取难、预报精度不足的问题,研究了热镀锌钢卷力学性能梯度提升树(gradient boosting decision tree,GBDT)预报模型。利用互信息差算法综合评估工艺参数、化学成分和钢卷尺寸参数等条件属性的相对重要性以及属性之间冗余性,进行模型条件属性筛选;采用同分布原理进行样本划分,结合网格搜索法和交叉验证法优化模型参数,建立力学性能GBDT预报模型。将GBDT模型预报结果与随机森林(random forest,RF)、AdaBoost算法和BP神经网络的预报结果进行比较,比较表明GBDT模型优于其他模型,90%的数据样本预测的绝对误差小于14.24 MPa,94.6%的数据样本相对误差在6%范围内,具有更高的预测精度。     

焊接电流对镁/镀锌钢 TIG熔--钎焊接头显微组织与力学性能的影响

采用TIG熔-钎焊焊接方法,以镁合金焊丝为填充材料,对镁合金与镀锌钢进行连接实验,并分析热输入量对接头显微组织和力学性能的影响.热输入量过小会阻碍镁/钢界面反应层的形成而使得焊缝难以焊合,热输入量过大又会促进焊缝内部脆性第二相的长大,降低接头力学性能.接头强度随着焊接电流和焊接速度的增大都呈现先上升后下降的趋势,电流为70 A时强度达到最大,该值接近AZ31B母材的88．7%.此时断裂发生于焊缝熔焊区,断面出现大量韧窝和撕裂棱,呈现出塑性断裂特征.     

TMCP工艺对Si--Mn系贝氏体钢组织与性能的影响

研究了轧后中温缓慢冷却与中温等温两种不同的热机械控制工艺( thermomechanical control process, TMCP)对硅锰系贝氏体钢的组织与性能的影响。通过拉伸试验机测试试验钢的力学性能,利用扫描电子显微镜、电子背散射衍射等分析手段对试验钢进行显微组织结构分析,并利用X射线衍射测定残余奥氏体含量。结果表明：随着轧后连续缓慢冷却开始温度的升高,贝氏体钢的抗拉强度、硬度及拉伸应变硬化指数n值有所提高,伸长率和冲击韧性降低,屈强比先降低后升高。随着轧后等温时间的延长,贝氏体钢的抗拉强度与屈强比先降低后升高,伸长率及冲击韧性先升高后降低。相对于等温制度,连续缓慢冷却可得到更好的综合力学性能,强塑积明显高于前者,伸长率比前者高20%以上。     

热处理工艺对高碳贝氏体钢组织与力学性能的影响

借助OM、SEM、XRD等手段,对比研究了一步、两步等温贝氏体转变工艺及QPB(淬火+配分+贝氏体转变)工艺对高碳贝氏体钢(w(C)=0.79%)显微组织与力学性能的影响。结果表明,采用一步等温贝氏体转变工艺处理试验钢时,当等温温度同为250℃,随着保温时间的延长,钢中贝氏体转变越充分,块状残余奥氏体尺寸降低,组织更为均匀细小;而在较低温度下(200℃)等温处理时,钢中残余奥氏体含量显著降低,贝氏体铁素体板条更细小,材料的强度和硬度提高,而塑性和韧性下降。两步等温贝氏体转变工艺处理(250℃×24 h+200℃×72 h)的试验钢中贝氏体铁素体板条平均尺寸约为82 nm,残余奥氏体体积分数为21.4%,获得了最佳的综合力学性能,抗拉强度达到2040 MPa,伸长率为12.5%,冲击韧性为21 J。QPB工艺提高了贝氏体转变速率,大大缩短了热处理时间,最终得到马氏体+贝氏体铁素体+残余奥氏体的组织,试验钢同时也获得了良好的强度和塑韧性。     

Effect of hot stamping parameters on the mechanical properties and microstructure of cold-rolled 22MnB5 steel strips

Thermomechanical experiments were carried out to reproduce the hot stamping process and to investigate the effects of process parameters on the microstructure and mechanical properties of stamped parts. The process parameters, such as austenitizing temperature, soaking time, initial deformation temperature and cooling rate, are studied. The resulting microstructures of specimens were observed and analyzed. To evaluate the mechanical properties of specimens, tensile and hardness tests were also performed at room temperature. The optimum parameters to achieve the highest tensile strength and the desired microstructure were acquired by comparing and analyzing the results. It is indicated that hot deformation changes the transformation characteristics of 22MnB5 steel. Austenite deformation promotes the austenite-to-ferrite transformation and elevates the critical cooling rate to induce a fully martensitic transformation.     

热处理工艺对低温贝氏体钢微观组织及力学性能的影响

利用SEM、EBSD、XRD及力学性能测试等手段,对比研究了一步、两步等温贝氏体转变及贝氏体转变+深冷处理工艺对低温贝氏体钢显微组织及力学性能的影响。结果表明,相较于一步等温贝氏体转变工艺,两步等温贝氏体及贝氏体转变+深冷处理均可降低钢中块状残余奥氏体含量,细化晶粒;与两步等温贝氏体转变相比,深冷处理可以极大缩短工艺时间,所得材料在获得相近强度的同时,会牺牲部分韧性;两步等温贝氏体处理后,试验钢强塑积达到了19.66GPa·%,U型冲击吸收功可达80J,其综合力学性能最优。     

回火工艺对热轧高强贝氏体钢轨组织和力学性能的影响

本文研究了不同回火工艺条件下热轧态U25CrNi高强贝氏体钢轨的组织与力学性能变化。结果表明,试验钢热轧态和回火组织均由贝氏体、马氏体和残余奥氏体构成。当回火条件为300℃×200min时,试验钢中部分残余奥氏体发生贝氏体相变,钢的各项力学性能变化不大;当回火温度升至400℃时,试验钢中残余奥氏体体积分数较大,碳化物析出量较少,内应力进一步释放,试验钢的延伸率和冲击吸收功达到最大值,同温度下延长回火时间至360min,钢中碳化物颗粒析出增多,延伸率和冲击性能明显降低;当回火温度为500℃时,试验钢中贝氏体铁素体明显粗化,并伴随大量碳化物颗粒析出,残余奥氏体大量分解,出现了回火脆性。综合考虑,U25CrNi热轧高强贝氏体钢轨的最佳回火工艺为400℃×200min。     

退火温度对退火马氏体基TRIP钢显微组织和力学性能的影响

将C-Si-Mn系TRIP钢通过完全淬火和两相区退火相结合的工艺,得到一种以退火马氏体为基体的TRIP钢(简称TAM钢),并对比分析了TAM钢在不同温度退火后的显微组织和力学性能.结果表明,TAM钢经退火后的显微组织特征为精细规整的板条退火马氏体基体、片状残余奥氏体和贝氏体/马氏体组成的混合组织.这种组织降低了基体的硬度以及基体和第二相之间的强度比,减少了基体的位错密度.随着退火温度的提高,退火马氏体基体的板条形态逐渐消失,新生马氏体/贝氏体的团状混合组织逐渐增多.当退火温度为780℃时,综合力学性能优异,抗拉强度为1130 MPa,延伸率可达20%,强塑积为22600 MPa·%.当退火温度较低时,残余奥氏体主要以片状存在于退火马氏体板条间,有利于TRIP效应的发生.     

淬火-回火工艺对X80管件钢组织性能的影响

采用扫描电子显微镜(SEM)、电子背散射衍射分析技术(EBSD)和透射电子显微镜(TEM)等实验手段,研究了不同淬火--回火热处理工艺制度对X80管件钢组织性能的影响.结果表明:一次930℃淬火后,随着回火温度的升高,实验钢屈服强度先升高后降低,在630℃达到最大值588MPa;抗拉强度随回火温度升高持续下降,680℃时降至630MPa.二次两相区淬火,经630℃回火后,X80管件钢有最佳的综合力学性能,-50℃冲击韧性显著提高,Ak达到210J.这是由于二次淬火温度在860℃两相区时,组织中奥氏体晶粒大幅细化,经630℃回火后,细晶马氏体组织中出现位错亚结构的回复软化、板条边界钝化和块状M-A组元分解产生的析出强化机制综合作用的结果.     

Ti对高强耐候钢力学性能的影响

通过光学显微镜、透射电镜(TEM)以及力学性能测试等手段分析了薄板坯连铸连轧(TSCR)工艺生产Ti微合金化高强耐候钢的成分及工艺对显微组织和力学性能的影响.研究结果表明:钢中加入Ti,屈服强度有明显的提高;钛质量分数为0.05%～0.08%时,高强耐候钢的晶粒尺寸随着钛含量的增加基本不变;高强耐候钢强度的提高主要取决于钢中有效钛的含量,有效钛不仅与钛的含量有关,而且还与S, N的含量有关;在有效钛含量一定的条件下,析出强化的大小主要取决于轧后的卷取温度.     

医用不锈钢表面TiN薄膜的组织结构和力学性能研究

为改善医用不锈钢的耐磨性,采用反应磁控溅射在304不锈钢表面沉积了TiN薄膜,研究了Ti过渡层沉积时间对TiN薄膜微观结构和力学性能的影响。通过Ｘ射线衍射仪、扫描电子显微镜、纳米压痕仪、FST1000型薄膜应力测试仪、HSR-2M摩擦磨损试验机和WS-2005型涂层附着力自动划痕仪对样品进行微观组织表征和力学性能测试。结果表明,当Ti过渡层沉积时间为20 min,Ti过渡层厚度为340 nm时,TiN薄膜结晶性最强,硬度和弹性模量达到最大值,分别为21.6 GPa和327.5 GPa,平均摩擦因数达到最小值0.45,临界载荷达到最大值24.7 N,TiN薄膜的力学性能、摩擦性能以及与基体的结合力达到最优。进一步延长Ti过渡层的沉积时间,TiN薄膜的柱状晶组织粗化、力学性能、摩擦性能以及与基体的结合力均降低。