石墨和碳化物形态对高镍奥氏体球铁抗热冲击性能的影响

本文论述了合金元素Si,Cr,Mo对含Ni20％的高镍奥氏体球墨铸铁抗热冲击性能的影响,揭示了石墨和碳化物形态与热冲击疲劳裂纹扩展方式和扩展速率之间的关系。发现石墨呈球状时热冲击疲劳裂纹为晶界型裂纹,抗热冲击性能最好;呈片状时为穿晶型裂纹,抗热冲击性能最差,呈枝晶状时为(晶界加穿晶)混合型裂纹,抗热冲击性能介于前二者之间.加入适量的Cr,Mo,Si可显著地提高抗热冲击性能。     

FeMnSi基形状记忆合金在水溶液中的电化学腐蚀

在 Fe Mn Si基形状记忆合金中加入 N,能强化基体 ,改善其形状回复率 ,同时有可能提高抗腐蚀性能 .采用浸泡试验和慢线性电位扫描法测量阳极极化曲线等方法 ,以 1 Cr1 8Ni9Ti不锈钢为参照 ,研究了 Fe Mn Si、Fe Mn Si Cr、Fe Mn Si Cr N等合金在 Na Cl(w=3 .5 % )、Na OH(3 mol/L )、HCl(1 mol/L)溶液中的电化学腐蚀行为 .结果表明 :在 Na Cl和 HCl溶液中 ,Fe Mn Si Cr N的抗腐蚀性能较好 ,但不如 1 Cr1 8Ni9Ti;Na OH溶液中 ,Fe Mn Si三元合金会发生钝化 ,且有很宽的钝化区 ,因此有很好的抗腐蚀性能 ,而抗腐蚀性能排序为 Fe Mn Si>Fe Mn Si Cr N>Fe Mn Si Cr>1 Cr1 8Ni9Ti.总之 ,与 Fe Mn Si和 Fe Mn Si Cr相比 ,Fe Mn Si Cr N在水溶液中有较好的抗腐蚀性能     

定向凝固镍基DZ792及DZ792G合金的高温热腐蚀行为

采用涂盐法研究了DZ792与DZ792G合金涂覆75%Na2SO4+25%NaCl混合盐后在900℃下的热腐蚀行为与机理.结果表明,900℃涂盐腐蚀条件下DZ792与DZ792G合金的热腐蚀机制为“酸/碱盐溶-内硫化氧化”.DZ792G合金在热腐蚀70~150h,腐蚀机制由碱性盐溶机制转化为酸性盐溶机制,最终导致灾难性腐蚀.DZ792G合金因具有较高的Ti含量,合金表面氧化膜的外侧形成富Ti氧化物层,TiO2与熔盐反应消耗其中的O2-,促进热腐蚀由碱性向酸性盐溶机制转变.而DZ792合金Ti含量较低,TiO2层在氧化膜内侧形成,外侧少量Ti氧化物形成稳定的NiTiO3尖晶石层.DZ792合金氧化膜外侧的富Cr2O3层与熔盐直接反应,抑制了热腐蚀反应,因而具有优异的抗热腐蚀能力.     

添加微量Si对锆合金耐腐蚀性能的影响

通过高压釜腐蚀实验研究了添加微量Si(0.02%)对Zr-1Nb(质量分数,%)和Zr-1Nb-0.8Sn-0.38Fe-0.1Cr合金在400℃/10.3 MPa过热蒸汽和360℃/18.6 MPa/0.01 mol/L LiOH水溶液中耐腐蚀性能的影响.利用透射电子显微镜(transmission electron microscope,TEM)观察了合金的显微组织.结果表明:添加微量Si对Zr-1Nb合金在两种水化学条件下的耐腐蚀性能影响不大;添加微量Si会使Zr-1Nb-0.8Sn-0.38Fe-0.1Cr合金在400℃/10.3 MPa过热蒸汽中的耐腐蚀性能变差,但对其在360℃/18.6 MPa/0.01 mol/L LiOH水溶液中的耐腐蚀性能影响不大.这说明Si对不同的合金在不同水化学条件下耐腐蚀性能的影响规律是不同的.在Zr-1Nb和Zr-1Nb-0.8Sn-0.38Fe-0.1Cr中添加0.02%Si后分别发现了尺寸较大的Zr5Si4第二相(second phase particles,SPPs)和Zr(Nb,Fe,Cr,Si)2第二相,这会对锆合金的耐腐蚀性能产生不利影响.     

应用于热浸镀55%铝锌合金锅体材料的研究

介绍了一种自制的Si—Cr合金铸铁在热浸镀55％铝锌合金中浸镀的腐蚀情况，研究了该种铸铁的腐蚀动力学及其耐蚀机理，证明了自制的Si—Cr合金铸铁适合于作为55％铝锌合金镀浴的锅体材料。     

定向凝固合金DZ466在涂 NaCl/Na2 SO4盐条件下热腐蚀行为

采用涂NaCl/Na2 SO4盐方法研究了DZ466合金在850℃和950℃条件下热腐蚀行为.结果表明：合金的腐蚀层包括三个区域,最外层为( Ni,Co) O氧化物层,次外层为尖晶石结构氧化层( Ni,Co) Cr2 O4,内层为内腐蚀层,850℃时该层为Ni3 S2,而950℃时除Ni3 S2外,在靠近次外层还形成内氧化Al2 O3;在850℃和950℃时合金的热腐蚀机制相同,氧化膜连续性的破坏,是合金遭受热腐蚀的主要原因;热腐蚀增重曲线均符合抛物线规律,其速率常数分别为3.1×10-11 g2·cm-4·s-1和1.5×10-9 g2·cm-4·s-1,热腐蚀激活能分别为179.2 kJ·mol-1和138.3 kJ·mol-1.     

Cu-Ni-Si基引线框架合金的组织和性能

设计了4种不同成分的引线框架铜合金,通过对比其硬度、强度、导电性以及软化温度等,分析了合金中P,Ni,Si,Cr合金元素对合金各性能的影响.研究结果表明:采用合理的热处理工艺可以使Cu-3Ni-0.6Si基合金在时效过程中析出尺寸在20～40 nm之间的δ-Ni2Si颗粒,使合金的强度和导电率达到良好的匹配;微量的P能有效地提高合金的强度、硬度和弹性模量,同时使Ni2Si析出颗粒的弥散度提高,尺寸减小,但会降低合金的导电率;少量的Cr能有效提高合金的强度和软化温度.     

Fe基非晶及纳米晶在硫酸中的腐蚀研究

利用电化学极化曲线的方法和电化学阻抗技术,研究非晶Fe78Si13B9和纳米晶Fe73.5Si13.5B9Nb3Cu1合金在1 mol·L-1的H2SO4溶液里的电化学腐蚀行为;利用X射线衍射仪和示差扫描量热计(DSC),研究该非晶薄带的非晶特性及晶化过程;用扫描电镜观察极化测试后的试样形貌;还研究不同的热处理温度对材料的结构及在1 mol·L-1的H2SO4溶液里耐腐蚀性能的影响.结果表明,纳米晶比非晶合金的耐腐蚀性能要好;随着热处理温度的升高,非晶的耐腐蚀性能得到提高,而纳米晶则降低.     

新型定向凝固高温合金750℃抗热腐蚀性能

研究了涂有75%Na2SO4+25%NaCl盐膜的新型定向凝固镍基高温合金在750℃的热腐蚀行为,采用X射线衍射仪和带能谱的扫描电镜分析腐蚀产物相组成以及微观结构.结果表明:该合金在开始阶段腐蚀速率较大,随着腐蚀时间的延长以及合金腐蚀层厚度的增加,腐蚀速率降低.腐蚀层可分为3个区域:外层是以TiO2和Cr2O3为主相对疏松的氧化层,中间层具有保护性的是富Cr层,内层是以Al,Ti为主的氧化物以及点状分布的硫化物.合金的热腐蚀主要由氧化-硫化共存伴随着表面腐蚀物挥发形成,在此过程中腐蚀持续向合金基体推进,使得腐蚀层不断增厚.     

K4169合金在模拟烟气环境中的热腐蚀行为

采用XRD、SEM、EDS以及EPMA等分析方法,研究铸态K4169合金及固溶-时效处理后K4169合金在650℃下模拟烟气(75%Na_2SO_4+25%NaCl)环境中的热腐蚀行为.结果表明:2种状态的K4169合金腐蚀动力学曲线均遵从抛物线规律;2种试样的腐蚀产物均分为2层,其内腐蚀层的腐蚀产物为Ni_3S_2;铸态合金的外腐蚀层产物分3部分:最外侧为Ni_3S_2薄层;中间以Fe_3O_4,NiO,NiFe_2O_4等氧化产物为主;内侧以Cr-O为主,有少量的铌、铝、钛的氧化物;固溶-时效态合金外腐蚀层的腐蚀产物为外侧以Fe_3O_4、NiO、NiFe_2O_4为主和内侧以Cr-O为主的2部分构成.2种状态合金的热腐蚀规律均遵循碱性机制.固溶-时效态试样的腐蚀层厚度低于铸态试样,固溶-时效处理能显著提高K4169合金的抗热腐蚀能力.     

高温挥发性对镁铬砖抗渣侵性能的影响

研究TH法用镁铬砖中不氧化铬含珠镁铬砖的高温挥发失重对镁铬砖抗渣侵性能的影响 .研究结果表明 ,氧化铬含量较低的镁铬砖高温挥发对使用性能的影响并不严重 ;提高镁铬砖中的氧化铬的含量 ,有利于在熔渣侵蚀时增加熔渣的粘度 ,抑制熔渣向砖内的侵蚀 .当Cr2 O3 >2 0 %时镁铬砖的组织劣化严重 ,抗渣侵蚀能力降低     

合金元素Cr对LaNi5基Ni/MH电极性能的影响

测定了LaNi5基储氢合金的相成分,晶体结构和电化学性能.电化学测试是以合金粉制成负极,以烧结Ni(OH)2为正极,以6mol/L KOH溶液为电解液,制成开口式MH-Ni二次电池,在室温下测定的.结果显示,Cr部分替代LaNi4.7Si0.3合金中的Si形成的LaNi4.7Si0.3-xCrx合金均为CaCu5结构,未改变原合金的晶体结构.其中LaNi4.7Si0.22Cr0.08合金具有较高的放电容量,较好的放电平台和较快的活化速度.小电流放电性能比大电流放电好.     

Corrosion-wear behavior of nanocrystalline Fe_(88)Si_(12) alloy in acid and alkaline solutions

The corrosion-wear behavior of a nanocrystalline Fe_(88)Si_(12) alloy disc coupled with a Si_3N_4 ball was investigated in acid(pH 3) and alkaline(pH 9) aqueous solutions. The dry wear was also measured for reference. The average friction coefficient of Fe_(88)Si_(12) alloy in the pH 9 solution was approximately 0.2, which was lower than those observed for Fe_(88)Si_(12) alloy in the pH 3 solution and in the case of dry wear. The fluctuation of the friction coefficient of samples subjected to the pH 9 solution also showed similar characteristics. The wear rate in the pH 9 solution slightly increased with increasing applied load. The wear rate was approximately one order of magnitude less than that in the pH 3 solution and was far lower than that in the case of dry wear, especially at high applied load. The wear traces of Fe_(88)Si_(12) alloy under different wear conditions were examined and analyzed by scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy. The results indicated that the tribo-chemical reactions that involve oxidation of the worn surface and hydrolysis of the Si_3N_4 ball in the acid solution were restricted in the pH 9 aqueous solution. Thus, water lubrication can effectively improve the wear resistance of nanocrystalline Fe_(88)Si_(12) alloy in the pH 9 aqueous solution.     

磨粒粒径对Si3N4结构陶瓷冲蚀磨损性能的影响

以冲蚀磨损工况下的典型应用材料Cr15Mo3高铬铸铁为对比材料,采用转盘式液-固双相流试验机研究了不同SiC磨粒粒径对Si3N4结构陶瓷抗冲蚀磨损性能的影响,分析了试验材料冲蚀磨损的微观失效机制.研究结果表明:在各种粒径磨粒的冲蚀磨损条件下,Cr15Mo3铸铁的冲蚀磨损率都比Si3N4结构陶瓷的高,Si3N4结构陶瓷的抗冲蚀磨损能力是Cr15Mo3铸铁的20倍左右;粗颗粒磨料冲蚀条件下试验材料的体积损失比细颗粒磨料冲蚀条件下的大,即磨粒越粗冲蚀磨损越严重;在微观上,Cr15Mo3的腐蚀坑、冲蚀坑多,基体材料冲刷磨损严重,W型失效形貌明显,而Si3N4结构陶瓷的冲蚀磨损面比较光滑,材料失效主要是晶界粘结相失去多所致;结构致密、晶粒细小并有细小柱状晶的存在等是Si3N4结构陶瓷抗冲蚀磨损性能优异的主要原因.     

Co66Ni6Fe6Cr1Si10B11的晶化动力学研究

本文通过用压力式膨胀仪对Co_(66)Ni_6Fe_6Cr_1Si_(10)B_(11)非晶合金进行了晶化动力学研究表明,晶化过程在膨胀曲线上反映清晰,有良好的再现性;其结果与热分析法、电阻法的结果相符合.晶化过程分三个阶段,在每一阶段的峰值温度时的晶化激活能分别为568×10~3、405.0×10~3和321.3×10~3J/mol,晶化相分别为Co(4F)、Fe_(4.5)Ni_(18.5)-B_e、FeSi_2、CO_2Si及一个尚未鉴定的相.     

钢表面化学气相沉积碳化硅及其高温腐蚀行为

研究了耐热钢表面化学气相沉积碳化硅的工艺．比较了耐热钢、碳化钛膜和碳化钛／碳化硅双层膜在O2 Br2 Ar气氛中的高温腐蚀行为，通过热力学分析，解释了腐蚀动力学现象．证明了在耐热钢表面被覆碳化钛／碳化硅双层膜可以大幅度提高其抗高温腐蚀能力。     

高含CO2油田腐蚀环境下16Mn管线钢电化学腐蚀行为

油田开发生产中，高CO2环境会引起集输管线严重腐蚀。为了给高CO2环境腐蚀防护方案提供技术依据，通过动电位极化扫描和电化学阻抗测试研究了温度、溶解O2对16Mn管线钢在高含CO2腐蚀环境下电化学腐蚀行为的影响。结果表明：随着温度的升高，16Mn钢的腐蚀电位减小，腐蚀倾向性增强，但腐蚀电流密度大大减小，表现出较好的抗温耐蚀性能；同样温度下，16Mn钢在饱和O2环境中相比不含O2时极化曲线的腐蚀电流密度减小，交流阻抗谱的电荷传递电阻大大增加，且低温时更显著，表现出较好的低温抗氧耐蚀性能。     

铁基金属玻璃涂层在无铅钎料中的耐腐蚀性及机理

选用Fe基非晶合金粉末(含有Cr、Mo、Ni、P、B、Si),采用等离子喷涂方法在Q235基体上制备了金属玻璃涂层.在自行设计的腐蚀实验装置中将Q235钢、1Cr18Ni9Ti不锈钢和覆有Fe基金属玻璃涂层的Q235钢浸入450,℃的高温液态无铅钎料Sn-3.5,Ag-0.5,Cu中进行腐蚀,利用扫描电子显微镜微观分析了腐蚀后的微观形貌及腐蚀产物.研究结果表明:相同实验条件下,Q235钢和1Cr18Ni9Ti不锈钢表面均腐蚀严重,断面微观组织分为钎料层、腐蚀层和基体层.其中Q235钢的腐蚀剧烈,腐蚀层成分为FeSn2;1Cr18Ni9Ti不锈钢腐蚀较严重,腐蚀层成分为(Fe,Cr)Sn2.Q235基体表面的Fe基金属玻璃涂层腐蚀前后断面微观形貌变化不大,没有出现明显的腐蚀分层,表现出了非常好的耐高温无铅钎料腐蚀的能力.     

新型弹簧钢35SiMnB松驰抗力的研究

采用拉、压Bauschinger效应实验法、载荷松驰法和循环应力松驰法对新型弹簧钢35SiMnB松驰抗力及其临界区处理的影响进行了研究,并和常用弹簧钢60Si_2Mn进行了对比。结果表明:以迴线面积所表征的35SiMnB的松驰抗力略低于60Si_2Mn;但临界区热处理可以大幅度提高35SiMnB的迴线面积,同Bauschinger应变一样,迴线面积表征了相间应力或长程内应力的高低,循环变形量和载荷松驰量两个钢相当。文中对用迴线面积作为松驰抗力的表征参量的适用条件及迴线面积的测试方法提出了建议。     

喷丸及退火处理对1Cr18Ni9Ti合金抗高温氧化性能的影响

研究了经过喷丸处理及400℃退火处理的1Cr18Ni9Ti合金试样在900℃空气中的循环氧化性能。经SEM,EDS分析及氧化动力学研究发现:喷丸处理虽然促进了铬的选择性氧化,但却使合金表面的压应力增大,所形成的氧化膜的抗剥落性能也不好;退火处理不仅使喷丸试样表面的应力得以消除,并且起到了低温预氧化的作用。经过退火处理的合金表面形成了附着性良好的选择性氧化铬膜,其氧化增重与氧化膜剥落量下降,起到了很好的保护作用,提高了合金的抗高温氧化性能。