摩擦焊接中热处理工艺的研究

针对摩擦焊接后融合区韧性差的缺陷,采取5种热处理工艺对试件进行金相组织观察及机械性能试验,试验结果表明焊后正火再调质热处理工艺更能提高摩擦焊区的综合力学性能,平均抗拉强度为691 MPa,平均延伸率为18.6%,平均冲击值为40 J/cm2.     

V的碳氮化合物析出对36Mn2V非调质钢组织性能的影响

在φ340机组上进行非调质36Mn2V和37Mn5油井管钢工艺试验,对比分析二者组织性能,研究36Mn2V钢中微合金元素V的碳氮化物析出对其组织性能的影响。结果表明,36Mn2V、37Mn5钢可分别用于高钢级N80-1和低钢级J55、K55油井管的生产,36Mn2V非调质钢在高温形变诱导下析出V(C、N),促进了晶内细小铁素体和珠光体的析出,反之细晶铁素体析出促进了V(C、N)沿γ/α界面弥散析出,故而显著改善了36Mn2V非调质钢组织性能。     

热变形温度对先共析铁素体等温转变动力学的影响

试验研究了一种Cr－Mn－Mo－B低碳低合金高强钢奥氏作热变形温度对相变前奥氏体组织状态及对先共析铁素体等温转变动力学的影响，结果表明，随着奥氏体热变形温度的降低，相变前奥氏体晶粒减小，并且先共析铁素体等温转变孕育期缩短，先共析铁素体转变量增多．     

Ti对C-Mn-V非调质钢组织与性能的影响

研究了 Ti含量和锻造工艺对 C-Mn-V 非调质钢组织与性能的影响,并把实验钢的性能与调质中碳钢进行比较。分析了含Ti 钢的显微组织特点,讨论了钢的组织与性能之间的关系.结果表明:加入少量的 Ti可以改善钢的显微组织,提高韧性,但加入过量(>0.044％)反而会使韧性下降。钢的强化因素是以 70％—80％的珠光体为主。钢中 Ti的最佳含量为0.02％。此外还计算了各组织因素对强度的贡献。     

非调质钢中钛氧化物冶金行为

通过热力学计算及实验,研究了含钛汽车用非调质钢在液态和凝固过程中含钛夹杂物的析出规律.研究表明,通过调整非调质钢中O,Al和Ti的含量,可以控制夹杂的形态和尺寸,从而得到细小、弥散非金属夹杂物作为针状铁素体的形核核心,细化钢的组织,提高钢的强度和韧性.     

Fe-C-X系合金针状铁素体在奥氏体贫碳区先共析转变的热力学分析

针状铁素体组织强度高、韧性好,基于氧化物夹杂形核,有很强的自身细化晶粒的能力,获得大量超细针状铁素体组织是超级钢研究的主要发展方向.建立了Fe-C-X系合金针状铁素体在奥氏体贫碳区先共析转变的热力学模型,并对Q235钢进行了数值模拟.结果表明,针状铁素体在实际相变开始温度(约923 K)的相变驱动力(绝对值)为450～740 J/mol,而且随着贫碳区碳含量的减少而增加.该模型可获得比以往扩散模型更大的相变驱动力,从热力学角度来讲,针状铁素体在奥氏体贫碳区很可能具有先共析转变的相变过程.     

风电塔架Q345E钢板焊接接头的组织与力学性能

风电塔架作为风力发电机的重要支撑部件,其焊接接头性能对风机安全服役至关重要.针对该问题,采用金相、硬度、室温拉伸和断口分析等方法研究手工电弧焊和MAG焊工艺焊接风电塔架Q345E钢板的组织和力学性能.结果表明,不同焊接工艺下Q345E钢板焊接接头的组织与力学性能有明显差异,MAG焊的微观组织主要由较细小的先共析铁素体和珠光体构成,综合力学性能好;而手工电弧焊主要由较为粗大的块状铁素体和珠光体构成,且存在典型的铁素体魏氏组织,力学性能差.通过本研究证实MAG焊比手工电弧焊更适合于风电塔架的焊接.     

非调质钢磨削淬硬表面强化试验

与淬回火调质钢相比,空冷非调质钢不但能减低成本,而且可避免热处理所引起的零件变形.磨削强化处理技术是利用磨削热替代高、中频感应淬火热源对钢件表层进行强化处理,将磨削加工与表面强化合为一体.针对非调质钢进行磨削强化研究,通过变切深和变进给磨削强化试验,研究强化层深度的变化规律,对试件的金相组织进行分析.研究结果表明非调质钢磨削强化是可行性的,研究结论为进一步研究非调质钢磨削强化工艺打下了基础.     

Fe-C-X系合金针状铁素体在奥氏体贫碳区先共析转变的热力学分析

针状铁素体组织强度高、韧性好，基于氧化物夹杂形核，有很强的自身细化晶粒的能力，获得大量超细针状铁素体组织是超级钢研究的主要发展方向。建立了Fe—C-X系合金针状铁素体在奥氏体贫碳区先共析转变的热力学模型，并对Q235钢进行了数值模拟。结果表明，针状铁素体在实际相变开始温度（约923K）的相变驱动力（绝对值）为450-740J／mol，而且随着贫碳区碳含量的减少而增加。该模型可获得比以往扩散模型更大的相变驱动力，从热力学角度来讲，针状铁素体在奥氏体贫碳区很可能具有先共析转变的相变过程。     

形变对12MnMoVN钢连续冷却转变的影响

奥氏体区形变使钢的连续冷却转变曲线向左上方移动;形变促进先共析铁素体转变,使先共析铁素体数量增加;形变还诱发珠光体转变。岛状组织转变动力学曲线形状与岛状组织的基体铁素体类型有关。     

冷却工艺对低碳Ti微合金化热轧超高强钢组织性能的影响

对实验钢采用低碳高Ti微合金化的成分设计,进行了控轧控冷实验,通过控制不同的冷速和卷取温度,研究了过冷度和原子扩散速率对钢组织演变及(Ti,Mo)C粒子的析出行为的影响.研究结果表明,冷速为30℃/s,卷取温度为420℃时,实验钢屈服强度大于690MPa,抗拉强度为820MPa,断后伸长率达18%,并具有良好的低温冲击韧性.显微组织性能研究表明,多边形铁素体、针状铁素体、细小M/A岛及弥散的(Ti,Mo)C析出粒子的混合组织可实现强度和韧性的良好匹配.     

590MPa级热轧V-N高强车轮钢组织性能控制

对一种低成本V-N微合金化钢进行了控轧控冷实验,探讨了相变机理与析出行为,并系统地研究了其综合力学性能.结果表明,显微组织为多边形铁素体、粒状贝氏体及少量的针状铁素体,纳米尺度V(C,N)析出质点弥散地分布于铁素体或贝氏体铁素体基体内部.抗拉强度615MPa实验钢具有优良的断后延伸率,冷弯性能合格,扩孔率达到95%,满足轮辐用钢的加工要求,低温冲击性能良好.细晶强化、位错强化、析出强化、相变强化为主要强化机制.     

超快速冷却对中碳钢组织和性能的影响

利用超快速冷却装置,通过控制轧后冷却路径,对某中碳钢的显微组织和力学性能进行了系统的研究.结果表明:超快速冷却可以抑制先共析铁索体的生成,破坏原有先共析铁素体的网状分布;超快速冷却显著缩小了珠光体的片层间距;随着超快速冷却后温度的降低,实验钢的强度和室温冲击韧性同时得到了提高.高温终轧+超快速冷却工艺可以使中碳钢获得良...     

Nb-Ti微合金化热轧多相钢的组织和性能

通过两阶段控轧和随后的三段冷却,获得了14mm厚的Nb-Ti微合金化热轧多相钢板.利用光学显微镜、扫描电镜、透射电镜、X射线衍射(XRD)、电子背散射衍射(EBSD)和力学性能测试等手段对其组织和性能进行了研究.结果表明,试验钢的显微组织由铁素体、贝氏体和少量马氏体组成;其平均屈服强度为518MPa,抗拉强度为616MPa,延伸率高达41%;组织中大量的铁素体大角度晶界、近似等轴状铁素体晶粒和较小尺寸贝氏体束的存在,大大提高了试验钢的塑性;铁素体和贝氏体组织的细化,细小的(Nb,Ti)C粒子以及铁素体晶粒和贝氏体板条内的位错提高了试验钢的强度.     

添加或未添加 Cu?Nb 的超低碳高强度钢焊接金属的显微组织和力学性能

Two types of ultralow carbon steel weld metals (with and without added Cu?Nb) were prepared using gas metal arc welding (GMAW) to investigate the correlation between the microstructure and mechanical properties of weld metals. The results of microstructure characterization showed that the weld metal without Cu?Nb was mainly composed of acicular ferrite (AF), lath bainite (LB), and granular bainite (GB). In contrast, adding Cu?Nb to the weld metal caused an evident transformation of martensite and grain coarsening. Both weld metals had a high tensile strength (more than 950 MPa) and more than 17% elongation; however, their values of toughness deviated greatly, with a difference of approximately 40 J at ?50°C. Analysis of the morphologies of the fracture surfaces and secondary cracks further revealed the correlation between the microstructure and mechanical properties. The effects of adding Cu and Nb on the microstructure and mechanical properties of the weld metal are discussed; the indication is that adding Cu?Nb increases the hardenability and grain size of the weld metal and thus deteriorates the toughness.     

V-N微合金化X80抗大变形管线钢的组织与力学性能

通过热模拟试验机研究了V-N微合金钢过冷奥氏体动态连续冷却相变行为,设计了V-N微合金化X80抗大变形管线钢的轧制与冷却工艺参数并分析了组织和力学性能的关系.结果表明,动态CCT曲线出现高温转变区和中温转变区分离的现象,转变温度范围分别是637~728℃和441~601℃,当冷速为10~20℃/s时,形成针状铁素体为主的组织.V-N微合金化管线钢组织以多边形铁素体和针状铁素体为主,屈服强度、抗拉强度、均匀延伸率和-20℃夏比冲击功分别为603MPa,724MPa,11.1%和214J,满足API Spec 5L对X80管线钢的力学性能要求,同时具有好的强塑性匹配.     

微合金钢中氧化物夹杂对焊接热影响区组织、性能的影响

研究了一种微合金钢中夹杂物与模拟焊接热影响区微观组织以及低温冲击韧性的关系.结果发现:实验钢夹杂物以类球状Ti2O3-Al2O3-MnS型复合夹杂为主,分布较为均匀且尺寸小于3μm;在相变冷却时间较短(T8/5=40s)时,试样微观组织以针状铁素体和沿晶铁素体为主,板条贝氏体束较少,原奥氏体晶粒尺寸在50μm左右,低温冲击性能优良;随着相变冷却时间的延长(T8/5=60,80s),原奥氏体晶粒尺寸也随之增大,相变温度的提高和相变区域的变宽使得位于原奥氏体晶界附近的夹杂物对晶界处多边形铁素体的诱导促进作用更加明显,沿晶铁素体长大剧烈,一定程度上消耗了晶内针状铁素体对组织的分割细化作用,使得低温冲击韧性有所降低.     

微合金化非调质钢35MnVN低温冲击韧性研究

本研究通过对35MnVN钢低温系列冲击韧性值测定,金相组织分析、断口形貌与二次裂纹扩展途径观察,初步揭示了其低温冲击韧性的变化规律及影响因素。结果表明:铁素体晶粒尺寸及相对量、原奥氏体晶粒大小、珠光体团尺寸对低温冲击韧性值有较大影响;铁素体晶粒尺寸为较敏感因素;温度降低,晶界有弱化趋势。本文还讨论了改善低温冲击韧性的途径。     

X80管线钢的组织与性能研究

利用光学显微镜、扫描电镜、透射电子显微镜等对X80级别管线钢的组织与性能进行了研究.实验结果表明,通过控轧控冷工艺轧制的16 mm厚的X80管线钢的屈服强度达到670 MPa以上时,其屈强比低于0.85,韧脆转变温度低于-60℃,达到了很好的强韧性匹配.细化的针状铁素体有效地改善了实验钢的强度及韧性.X80管线钢中存在两种典型的析出物,一种以Nb,Ti(CN)为主,尺寸较大(50~200 nm);另一种以NbC为主,尺寸细小(小于30 nm).这些纳米级析出物对钢的组织细化和强化起到了重要作用.     

Toughening mechanisms of a high-strength acicular ferrite steel heavy plate

An ultra-low carbon acicular ferrite steel heavy plate was obtained with an advanced thermo-mechanical control process-relaxed precipitation controlled transformation (TMCP-RPC) at Xiangtan Steel, Valin Group. The heavy plate has a tensile strength of approximately 600 MPa with a lower yield ratio. The impact toughness of the heavy plate achieves 280 J at -40℃. The fine-grained mixed microstructures of the heavy plate mainly consist of acicular ferrite, granular bainite, and polygonal ferrite. The high strength and excellent toughness of the heavy plate are attributed to the formation of acicular ferrite microstructure. The prevention of blocks of martensite/retained austenite (M/A) and the higher cleanness are also responsible for the superior toughness.