对SiMnCr试验用钢,分别进行了淬火、等温淬火和空冷处理,并分别利用金相显微镜、扫描电子显微镜和透射电子显微镜进行了显微组织观察,测定了CCT曲线.淬火态下获得板条马氏体和其间的残余奥氏体薄膜组织,等温淬火得到准贝氏体组织,锻造空冷状态下得到以板条马氏体为主含贝氏体和少量位于板条间界的残余奥氏体薄膜复合组织,经300℃回火,无渗碳体析出.     

SiMnCr系高强度钢组织转变研究

对SiMnCr试验用钢，分别进行了淬火、等温淬火和空冷处理，并分别利用金相显微镜，扫描电子显微镜和透射电子显微镜进行了显微组织观察，测定了CCT曲线，淬火态下获得板条马氏体和其间的残余奥氏体薄膜组织，等温淬火得到贝氏体组织，锻造空冷状态下得到的以板条马氏体为主含贝氏体和少量位于板条间界的残余奥氏体薄膜复合组织，经300℃回火，无渗碳体析出。     

热处理工艺对高碳贝氏体钢组织与力学性能的影响

借助OM、SEM、XRD等手段,对比研究了一步、两步等温贝氏体转变工艺及QPB(淬火+配分+贝氏体转变)工艺对高碳贝氏体钢(w(C)=0.79%)显微组织与力学性能的影响。结果表明,采用一步等温贝氏体转变工艺处理试验钢时,当等温温度同为250℃,随着保温时间的延长,钢中贝氏体转变越充分,块状残余奥氏体尺寸降低,组织更为均匀细小;而在较低温度下(200℃)等温处理时,钢中残余奥氏体含量显著降低,贝氏体铁素体板条更细小,材料的强度和硬度提高,而塑性和韧性下降。两步等温贝氏体转变工艺处理(250℃×24 h+200℃×72 h)的试验钢中贝氏体铁素体板条平均尺寸约为82 nm,残余奥氏体体积分数为21.4%,获得了最佳的综合力学性能,抗拉强度达到2040 MPa,伸长率为12.5%,冲击韧性为21 J。QPB工艺提高了贝氏体转变速率,大大缩短了热处理时间,最终得到马氏体+贝氏体铁素体+残余奥氏体的组织,试验钢同时也获得了良好的强度和塑韧性。     

回火工艺对热轧高强贝氏体钢轨组织和力学性能的影响

本文研究了不同回火工艺条件下热轧态U25CrNi高强贝氏体钢轨的组织与力学性能变化。结果表明,试验钢热轧态和回火组织均由贝氏体、马氏体和残余奥氏体构成。当回火条件为300℃×200min时,试验钢中部分残余奥氏体发生贝氏体相变,钢的各项力学性能变化不大;当回火温度升至400℃时,试验钢中残余奥氏体体积分数较大,碳化物析出量较少,内应力进一步释放,试验钢的延伸率和冲击吸收功达到最大值,同温度下延长回火时间至360min,钢中碳化物颗粒析出增多,延伸率和冲击性能明显降低;当回火温度为500℃时,试验钢中贝氏体铁素体明显粗化,并伴随大量碳化物颗粒析出,残余奥氏体大量分解,出现了回火脆性。综合考虑,U25CrNi热轧高强贝氏体钢轨的最佳回火工艺为400℃×200min。     

亚稳奥氏体对高强度海洋工程用钢力学性能的影响

采用力学性能测试、组织观察等方法研究临界退火和不同温度回火对海洋工程用钢显微组织和力学性能的影响.结果表明,实验钢经两相区退火和不同温度回火后,获得了回火马氏体及不同体积分数(0~6%)的残余奥氏体.随实验钢中残余奥氏体体积分数的增加,屈服强度从753MPa降低到506MPa,抗拉强度介于794~843MPa,屈强比从0.9降低到0.6,延伸率从31.3%提高到36.2%.实验钢中残余奥氏体能够提高冲击塑性变形能力并阻碍裂纹扩展,在-80℃冲击功达到236J,然而热稳定性差的残余奥氏体在低温下优先转变成马氏体并降低了低温韧性,冲击功下降到136J.     

淬火介质对耐磨铸钢组织和性能的影响

分别研究了以水和机油作为淬火介质的42CrMo钢和双相耐磨钢淬火+回火后的显微组织和性能.确定了双相耐磨钢和42CrMo钢的最佳热处理工艺及性能.结果表明:双相耐磨钢经水淬和油淬回火后的显微组织均为板条马氏体+针状贝氏体+碳化物;42CrMo钢经水淬和油淬回火后的显微组织分别为回火马氏体+残余奥氏体和回火马氏体+铁素体+贝氏体.经过480h的低应力磨料磨损实验发现,水淬+280℃回火处理的42CrMo钢耐磨性能最好,其相对耐磨性可达高锰钢的1.558倍.     

回火温度对1500MPa级直接淬火钢组织与性能的影响

设计了一种新型1500MPa级Si-Mn-Cr-Ni-Mo多组元系低合金、超高强度工程结构钢,研究了回火温度对直接淬火钢组织与力学性能的影响.结果表明,抗拉强度随回火温度的升高而不断降低,屈服强度随回火温度升高先升高后下降,延伸率和冲击功均随回火温度升高呈现先升高、后降低、再升高的变化趋势.分析认为,回火过程组织演变的物理机制一方面包括板条马氏体和位错亚结构的回复、再结晶软化过程,另一方面包括残余奥氏体的分解与马氏体中过饱和碳的脱溶及析出第2相的强化机制综合作用.250℃回火后,板条马氏体内析出ε碳化物;400℃回火后ε碳化物明显粗化,产生回火脆性;600℃回火后部分析出相在奥氏体中形核,在马氏体基体内长大和粗化,最终形态为近似球形,另一部分析出相在马氏体内形核、生长,呈现椭球形或矩形.     

DQ-T工艺对12MnNiVR钢组织和力学性能的影响

研究了轧后在线淬火+离线回火(DQ-T)对12MnNiVR容器钢显微组织及力学性能的影响.结果表明,在线淬火至300℃获得的组织以条状贝氏体为主,淬火至30℃的组织为马氏体加贝氏体.经离线回火,原始带状下贝氏体为回火索氏体替代,同时析出大量微小FexC粒子.在630~710℃区间,随着回火温度的升高,屈服强度和硬度急速降低,而低温韧性明显提升.回火时间增加,强度下降,韧性增强.在最佳DQ-T工艺条件下:容器钢的ReH为660MPa,Rm为700MPa,A为19.4%,Akv(-20℃)为104 J.     

电阻焊接用高强Q125级石油套管钢组织及其性能

设计了一种低合金含量的Q125级高强度石油套管用钢,研究了热处理工艺对实验钢组织和力学性能的影响．与870℃淬火＋500℃回火工艺相比,实验钢在850℃淬火＋500℃回火工艺下具有更好的强韧性配合．与870℃淬火相比,850℃淬火处理的奥氏体晶粒尺寸较小,使决定钢力学性能的晶区、板条束尺寸细化,因此其性能更优异．淬火温度对实验钢的析出行为影响不大．尺寸较大的TiN以及TiC和TiN复合析出物对奥氏体晶界起到钉扎作用,可以抑制奥氏体晶粒的长大;含有Mo的尺寸较小的TiC可以起到钉扎位错的作用,阻止位错移动,对强度的提高贡献很大．     

70Si3Mn钢中无碳化物贝氏体组织及其性能研究

70Si3Mn钢是传统的弹簧钢,其常规热处理工艺是油淬后中温回火得到屈氏体组织。本文对70Si3Mn钢进行等温淬火处理获得无碳化物贝氏体组织,比较了其经不同温度等温淬火处理后的组织与力学性能,并对其耐磨性进行了研究。结果表明,70Si3Mn钢在Ms以上10~30℃等温可得到无碳化物贝氏体组织,该组织由厚度为160 nm的贝氏体铁素体板条和残余奥氏体薄膜组成,它具有较高的强度和硬度、高的塑性和韧性等优异的综合力学性能,同时具有较好的耐磨性。     

V、Ta微合金化12Cr低活性F/M钢的优化设计

采用Thermo-Calc热力学模拟计算与实验相结合的方法,优化设计了一种V、Ta微合金化的低活性F/M钢12Cr3WVTa,经1 050℃水淬及780℃回火后对其显微组织及析出相进行光学显微镜、扫描电镜和透射电镜观察以及能谱分析.实验钢淬火回火后显微组织由回火马氏体和少量δ铁素体相组成,析出相主要为M23C6和MX相(M=V,Ta;X=C,N),其中M23C6主要分布于回火马氏体板条界和相界,而MX弥散析出于回火马氏体板条内以及δ铁素体内.实验钢室温和高温(600℃)拉伸力学性能良好,600℃下材料抗拉强度为507 MPa,屈服强度为402 MPa,满足超临界水冷堆用包壳管的拉伸性能要求.     

Effect of lower bainite/martensite/retained austenite triplex microstructure on the mechanical properties of a low-carbon steel with quenching and partitioning process

We present a study concerning Fe–0.176C–1.31Si–1.58Mn–0.26Al–0.3Cr (wt%) steel subjected to a quenching and partitioning (Q&P) process. The results of scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and tensile tests demonstrate that the microstructures primarily consist of lath martensite, retained austenite, lower bainite (LB), and a small amount of tempered martensite; moreover, few twin austenite grains were observed. In the microstructure, three types of retained austenite with different sizes and morphologies were observed: blocky retained austenite (~300 nm in width), film-like retained austenite (80–120 nm in width), and ultra- fine film-like retained austenite (30–40 nm in width). Because of the effect of the retained austenite/martensite/LB triplex microstructure, the specimens prepared using different quenching temperatures exhibit high ultimate tensile strength and yield strength. Furthermore, the strength effect of LB can partially counteract the decreasing strength effect of martensite. The formation of LB substantially reduces the amount of retained austenite. Analyses of the retained austenite and the amount of blocky retained austenite indicated that the carbon content is critical to the total elongation of Q&P steel.     

预处理组织对低碳钢IQ&P工艺下组织及性能影响

采用γ单相区和γ+α双相区轧制并淬火工艺以及双相区再加热-淬火-碳配分( IQ&P)工艺,研究预处理组织对低碳钢室温状态多相组织特征及力学性能的影响规律. 实验用低碳钢经两种工艺轧制并淬火处理,获得马氏体和马氏体+铁素体的预处理组织,再经双相区IQ&P工艺处理后均获得多相组织. 马氏体预处理钢的室温组织由板条状亚温铁素体、块状回火马氏体以及一定比例的针状未回火马氏体和8. 2%的针状残余奥氏体组成;马氏体+铁素体预处理钢由板条状亚温铁素体、块状和针状未回火马氏体以及14. 3%的短针状或块状残余奥氏体组成. 在相同的双相区IQ&P工艺参数下,预处理组织为马氏体的钢抗拉强度为770 MPa,伸长率为28%,其强塑积为21560 MPa·%;而预处理组织为马氏体+铁素体的钢抗拉强度为834 MPa,伸长率增大到36. 2%,强塑积达到30190 MPa·%,获得强度与塑性的优良结合.     

汽车用高强度Q&P钢的组织与力学性能

研究了0.21C--1.43Si--1.35Mn钢在两相区及完全奥氏体区采用QP(Quenching and Partitioning)工艺加热后的微观组织与力学性能.结果表明:两相区加热可获得马氏体、残余奥氏体和铁素体组织,钢的抗拉强度为1 013 MPa,延伸率为25%,强塑积为25 655 MPa.%;完全奥氏体区加热可获得马氏体和残余奥氏体组织,钢的抗拉强度为1 257 MPa,延伸率为17%,强塑积为21 454 MPa.%;QP钢中的马氏体主要为板条状,伴有大量位错,并且发现有少量孪晶马氏体,分析认为由配分过程后的淬火过程转变而来;通过QP工艺可得到体积分数高达10.67%的残余奥氏体,分布在板条马氏体间,呈薄膜状.     

回火温度对低碳贝氏体高强度钢组织性能的影响

利用光学显微镜、扫描电镜、透射电镜和力学性能试验机等手段,系统研究了不同回火温度下低碳贝氏体高强度钢的组织及力学性能变化.结果表明:回火后位错密度的变化、析出相的形态、板条贝氏体的合并粗化和M/A岛的分解是导致力学性能变化的主要原因.600℃回火后屈服强度较热轧态强度提高了35MPa,-40℃冲击功提高了49J,此回火温度下实验钢具有最佳的强韧性配合.回火后低碳贝氏体高强度钢韧性改善主要是由于粗大M/A岛的分解,细小弥散分布的M/A岛可有效阻止裂纹扩展,改善低温冲击韧性.     

回火温度对在线淬火Q690q桥梁钢显微组织和力学性能的影响

通过光学显微镜和扫描电镜观察了不同回火温度下在线淬火Q690q试验钢显微组织,并通过拉伸试验对其力学性能进行了测试.结果表明,在线淬火试验钢主要为板条贝氏体组织,在540~650℃回火,试验钢为回火索氏体组织(铁素体基体上分布着较多的碳化物颗粒).随着回火温度的升高,板条尺寸变大,碳化物颗粒析出数量增多,平均尺寸变大,大角度晶界数量增多.同时随着回火温度的升高,试验钢强度呈下降趋势,塑韧性呈上升趋势.620℃下试验钢的综合力学性能最佳,屈服和抗拉强度分别为878,992MPa,断后延伸率为20%,-40℃下冲击吸收功为143 J.     

热轧态与回火态 AH80 DB 低碳贝氏体钢组织与冲击韧性

采用光学显微镜、扫描电子显微镜和透射电子显微镜对热轧态和回火态AH80DB低碳贝氏体钢的显微组织、马氏体/奥氏体( M/A)岛、第二相的析出行为以及晶界取向差、有效晶粒尺寸进行研究,揭示回火后低碳贝氏体钢冲击韧性得到改善的原因.结果表明：两种试样的组织均由板条状贝氏体、粒状贝氏体和针状铁素体组成,其中回火态试样中针状铁素体组织较多.热轧态钢中存在较大尺寸M/A岛且呈方向性分布,大角度晶界比例占17.33%,有效晶粒尺寸为3.57μm;而回火态钢中M/A岛的尺寸较小,大角度晶界比例增加3.43%,有效晶粒尺寸减小0.56μm.热轧态钢中析出相主要是( Nb,Ti) C,尺寸在50~150 nm之间,回火态试样中析出较多细小的球状( Nb,Ti) C析出相,尺寸在10 nm左右.     

等温温度对超细贝氏体钢组织演变规律的影响

通过热膨胀试验研究实验钢的等温转变动力学,采用盐浴等温淬火工艺制备超细贝氏体组织,利用扫描电镜、透射电镜和X射线衍射仪定量分析工艺参数对微观组织结构的影响.结果显示:实验钢室温组织由大量超细板条状贝氏体铁素体和板条间分布的薄膜状奥氏体的复相组织构成,210℃等温淬火得到的贝氏体板条间距细化到约60 nm,硬度约为HBW610;实验钢的最终组织特征取决于发生贝氏体转变的等温温度和等温时间,等温温度越低时贝氏体转变完成需要的等温时间越长.