喷射沉积Al-20Si-5Fe-3Cu-1Mg合金的微观组织与力学性能

利用喷射沉积技术制备了Al－20Si－5Fe－3Cu-1Mg合金,借助扫描电镜（SEM）,X-射线衍射和拉伸试验等手段研究了喷射沉积合金的微观组织和力学性能,分析了Fe对合金挤压和热处理后的组织变化．拉伸试验结果表明,喷射沉积Al－20Si-5Fe-3Cu-1Mg合金具有比粉末冶金Al-20Si-3Cu-1Mg合金更高的高温（300℃）强度．     

喷射成形原位反应TiC/Al-Fe-V-Si复合材料的显微组织

使用X射线衍射（XRD)、光镜(OM）、电子扫描电镜(SEM)、透射电镜（TEM）等对在TiC／Al-Fe-V—Si合金中原位反应生成TiC的喷射沉积坯件的显微组织进行了分析和研究．结果表明，原位反应生成的TiC颗粒在喷射沉积过程中抑制了针状相的形成，改善了合金的显微组织，生成的TiC颗粒均匀地分布在合金基体中．     

Mn对喷射沉积Al-25Si-xFe-yMn合金中Fe相的影响

通过喷射沉积工艺制备了Al-25Si-xFe-yMn(Mn/Fe质量比在0～1之间)系列合金的沉积坯,利用SEM、XRD和EDX对这些沉积坯的微观组织进行分析.结果表明,添加Mn元素,将生成颗粒状的α-Al15(Fe,Mn)3Si2,取代了针状的δ-Al4FeSi2和β-Al5FeSi相,从而显著地改善高硅铝合金中的Fe相的形貌,并且随着Mn/Fe质量比的提高,沉积坯中颗粒状的α-Al15(Fe,Mn)3Si2含量也增加,而针状相的含量却减少,当Mn/Fe质量比增加到0.83或1时,在沉积坯中只发现颗粒状的α-Al15(Fe,Mn)3Si2.     

过共晶铝硅合金中Al-Si-Mn-Fe相的形态影响因素

在 Al- 2 2 % Si合金中分别加入 0 .96 % Fe,0 .6 7% Mn和 1% Fe,1.5 0 % Mn;用浇注不同厚度的试样并观察金相组织的方法 ,了解和比较了不同 Mn/ Fe比和不同冷却速度对于合金中 Al- Si- Mn- Fe相形态的影响。研究结果表明 ,随着 Mn含量和冷却速度的提高 ,针状铁相转变为粒状并得到细化。     

喷射沉积Al-Si-Fe-Mn-Cu-Mg合金的析出强化行为

利用热分析（DSC）,显微硬度测定和透射电子显微分析等手段研究了喷射沉积Al-20Si-5Fe-3Cu-1Mg合金的时效过程,结果表明,两种沉淀强化相S－Al2CuMg和σ-Al5Cu6Mg2从合金基体中析出,有效地提高了合金的室温强度和高温（300度）强度。     

喷射沉积Al-30wt%Si合金的凝固组织与耐磨性能

研究了喷射沉积Al-30wt%Si合金的凝固组织和耐磨性能,结果表明喷射沉积Al-30wt%Si合金的组织由Si相和α相组成,细小的Si相均匀分布在α基体中,沉积态组织中硅相尺寸比金属型铸造试样降低2个数量级。喷射沉积高硅铝合金具有优良的耐磨性。随着硅相尺寸的减小,高硅铝合金的磨损由剥落为主的机制转变为犁沟变形机制。     

旋压加工对喷射沉积Al-8.5Fe-1. 3V-1.7Si 合金挤压管组织和性能的影响

采用喷射沉积-热挤压工艺制备快速凝固Al-8.5Fe-1. 3V-1.7Si耐热合金管材,并通过强力热反旋压工艺将这些挤压管进行多道次减薄,制备薄壁管;利用金相显微组织观察、透射电镜分析、扫描电镜分析和力学拉伸试验等手段,研究强力热反旋压工艺对喷射沉积Al-8.5Fe-1.3V-1.7Si合金挤压管材显微组织和力学性能的影响.研究结果表明喷射沉积Al-8.5Fe-1.3V-1.7Si挤压管的显微组织呈纤维条带状,不同条带中Al12(Fe,V)3Si(体心立方,a≈1.260 nm)颗粒大小和分布形貌不同,甚至出现θ-Al13 Fe4(底心单斜,a=1.543 nm,b=0.812 nm,c=1.254 nm,β=107.43°)和Al8Fe2Si(六方,a=1.270 nm,c=2.620 nm)粗块状相;条带间残留着未充分破碎的氧化物和原始粉末界面;在强力旋压过程中,条带状组织发生畸变,氧化膜破碎,并重新分布,弱结合的残留原始粉末界面减少或消失,显微组织趋于连续、均匀;与其他挤压管材相比,喷射沉积Al-8.5Fe-1.3V-1.7Si合金旋压管材,力学性能明显提高,材料各向异性有所减弱.     

原位合成VC和TiC颗粒对Fe3Al基合金显微组织的影响

以Fe3Al金属间化合物作为基体,采用反应铸造法制备了含VC,TiC颗粒Fe3Al基合金并研究了颗粒相在Fe3Al合金中的形成机理及颗粒相的加入对Fe3Al基合金显微组织结构的影响。结果表明,TiCp在高温液态熔体中原位合成,且在基体中均匀分布,可以作为异质形核核心而细化Fe3Al基合金铸定组织,从而改善Fe3Al合金的热加工性能;VCp是在固相中形核并长大的,对铸态组织的细化作用下明显,但其对热加工后再结晶组织的细化作用甚于TiCp。     

喷射沉积AlFeVSi合金热暴露过程中相转变与沉积态组织特点

采用喷射沉积工艺制备快速凝固AlFeVSi合金薄片和沉积管坯,通过示差热分析、X射线衍射分析、金相显微组织观察、透射电镜组织观察、硬度测试等检测手段,研究了喷射沉积AlFeVSi合金快凝薄片在高温热暴露过程中的相变和组织演变规律,并分析了喷射沉积AlFeVSi合金坯组织特点。结果表明,喷射沉积AlFeVSi快凝薄片基本上为呈微胞状的过饱和α-Al固溶体。加热温度低于500℃时,在高温热暴露过程中微胞状结构发生分解,α-Al过饱和固溶体脱溶,形成α-Al Al12(Fe,V)3Si(bcc,a≈1.260 nm)弥散颗粒的分解产物,当温度高于500℃时,Al12(Fe,V)3Si颗粒粗化聚集,并以独立形核长大的方式生成θ-Al13Fe4块状相。随着热暴露温度升高,喷射沉积AlFeVSi合金薄片的硬度呈下降趋势。喷射沉积AlFeVSi坯主要由α-Al固溶体和Al12(Fe,V)3Si颗粒组成,但也存在少量含粗大片状或块状相的非快速凝固组织。     

喷射沉积成形合金及金属基复合材料力学性能

介绍了近年来北京科技大学在该领域的部分研究结果，重点介绍典型喷射沉积材料（Ｎｉ３Ａｌ金属间化合物为基的合金儿２６１８Ａｌ＋ＳｉＣ颗粒增强金属基复合材料）的显微组织和力学性能。     

喷射沉积Al-20Si-5Fe-3Cu-Mg

利用喷射沉积技术制备了Ａｌ－２０Ｓｉ－５Ｆｅ－３Ｃｕ－１Ｍｇ合金,借助扫描电镜（ＳＥＭ）,Ｘ－射线衍射和拉伸试验等手段研究了喷射沉积合金的微观组织和力学性能,分析了Ｆｅ对合金挤压和热处理后的组织变化,拉伸试验结果表明,喷射沉积Ａｌ－２０Ｓｉ－５Ｆｅ－３Ｃｕ－１Ｍｇ合金具有比粉末冶金Ａｌ－２０Ｓｉ－３Ｃｕ－１Ｍｇ合金更高的高温（３００℃）强度。     

压铸TiC/Al-9Si-1.4Cu-0.5Mg复合材料的拉伸性能

利用熔铸——原位反应和压铸成形技术制备了TiC/Al-9Si-1.4Cu-0.5Mg复材料,测试了复合材料的拉伸性能。结果表明：TiC/Al-9Si-1.4Cu-0.5Mg复合材料的室温极限拉伸强度为354MPa,比基体合金提高26%;260℃时复合材料的极限拉伸强度为272MPa,比基体合金提高46%。复合材料的延伸率与Al-9Si-1.4Cu-0.5Mg合金相当。讨论了进一步提高熔铸——原位反应TiC/Al-9Si-1.4Cu-0.5Mg复合材料拉伸强度的途径。     

Microstructural evolution and intermetallic formation in Al-8wt% Si-0.8wt% Fe alloy due to grain refiner and modifier additions

An alloy of Al-8wt% Si-0.8wt% Fe was cast in a metallic die, and its microstructural changes due to Ti-B refiner and Sr modifier additions were studied. Apart from usual refinement and modification of the microstructure, some mutual influences of the additives took place, and no mutual poisoning effects by these additives, in combined form, were observed. It was noticed that the dimensions of the iron-rich intermetallics were influenced by the additives causing them to become larger. The needle-shaped intermetallics that were obtained from refiner addition became thicker and longer when adding the modifier. It was also found that α-Al and eutectic silicon phases preferentially nucleate on different types of intermetallic compounds. The more iron content of the intermetallic compounds and the more changes in their dimensions occurred. Formation of the shrinkage porosities was also observed.     

交流磁场对Al-Fe合金凝固组织的影响

研究了交流磁场对Al-Fe合金中含铁相形态及分布的影响.近共晶Al-1.99%Fe(质量分数,下同)和亚共晶Al-0.90%Fe两种铝合金在3℃/min的冷却速率凝固过程中,施加强度为0.3 T,频率为20 Hz的交流磁场,并与未施加磁场的试样进行对比.实验结果表明,在这两种合金中,无论是先析出Al3Fe相还是先析出-αAl,施加交流磁场后,Al3Fe相均向试样的中心处富集.这是由于Al3Fe相的磁化率大于熔融铝基体的磁化率,使得Al3Fe相和铝基体相比受到指向样品轴线的更大的电磁力,从而导致其向试样中心处聚集.     

Ni-Al系合金中的逆马氏体相变

采用多功能内耗仪测量室温至400 °C过程中，油淬Ni 36Al二元合金以及Ni27Al-12Fe、Ni-21.2Al-20Fe和Ni-24Al-16Fe三元合金的内耗和相对动力学模量，并采用X射线衍射仪分析了合金的相组成.结果表明：油淬Ni-36Al合金具有完全马氏体结构，油淬Ni-21.2Al-20Fe合金中含少量马氏体和大量类似Ni3Al和Ni5Al3的金属间化合物；在相同的频率和升温速率条件下，油淬Ni-21.2Al-20Fe的内耗峰最高且最窄，其内耗峰所对应的温度最低，油淬Ni-36Al的内耗峰最低且最宽，其内耗峰所对应的温度最高，并随Fe含量的增加而降低，且与其当量Al（Aleq）含量有关；内耗峰高度与单位时间内马氏体（L10）转变为奥氏体（γ）的转变量有关，而总的转变量与转变时间（峰宽）有关.     

Al-Cr中间合金在熔融Al-Zn-Mg-Si-Fe镀液中的扩散反应研究

以Al-Cr中间合金锭和熔融Al-Zn-Mg-Si-Fe镀液为研究对象,研究了Al-Cr中间合金锭浸入含不同质量分数Fe的630 ℃熔融镀液15 h的扩散反应。使用扫描电子显微镜、能谱仪分析了扩散前后Al-Cr中间合金锭组织和成分的变化,同时研究了镀液中Fe质量分数对Cr溶解度的影响。研究发现,随着镀液中的Zn、Mg、Si、Fe长时间向Al-Cr锭内部扩散,Al-Cr锭中原有的Al基体的组织转变成了与镀液成分相近的组织,原有的富Cr第二相转变成了Al-Cr-Zn-Si相和Al-(Fe, Cr)-Si相。随着Al-Cr锭中的Cr向镀液扩散,镀液中Cr质量分数升高,并在5 h后达到饱和。由于Cr和Al、Fe、Si优先形成了Al-(Fe, Cr)-Si金属间化合物,因此镀液中的Fe显著降低了Cr元素的饱和溶解度,当镀液Fe质量分数由0.10%增加至0.42%时,镀液中Cr质量分数由0.047%～0.059%减少至0.012%～0.016%。     

热海水中热浸镀用锌及锌铝合金的电化学性能

为了定量比较不同热浸镀层用金属(或合金)在热海水中对钢铁基体的阴极保护作用,参照国标GB/T 17848-1999的要求对几种典型的热浸镀用锌及锌铝合金测试了50℃条件下的恒电流性能,计算了电流效率,观察了腐蚀产物脱落情况及腐蚀均匀性,并据此评价了它们的电化学保护性能.结果表明:Zn的电化学性能最好,Zn-55Al-1.6Si合金的电化学性能最差,Zn-5Al-0.1RE,Zn-5Al-0.5Mg,Zn-6Al-3Mg,Zn-11Al-0.2Si-3Mg,Zn-25Al-0.2Si-0.2Mg和Zn-25Al-0.2Si-0.2RE合金介于二者之间.     

Al-1.3Si-0.7Mg-0.7Cu-0.3Mn铝合金薄板在固溶处理过程中的组织转变

通过XRD,OM和TEM组织观察、织构测定等方法研究了冷轧Al-1.3Si-0.7Mg-0.7Cu-0.3Mn铝合金汽车车身板在固溶处理过程中其合金相、晶粒、织构组态的变化.结果表明:Al-1.3Si-0.7Mg-0.7Cu-0.3Mn合金冷轧薄板中存在Al9Fe0.84Mn2.16Si,Al95Fe4Cr和Al6Mn不可溶合金相及Al1.9CuMg4.1Si3.3和Mg2Si可溶合金相;尺寸小于1μm的可溶合金相在540℃盐浴固溶中保温12 min以上即可全部溶入基体;冷轧薄板在540℃固溶保温2 min即可完成再结晶,形成{001}〈310〉和{110}〈113〉再结晶织构,其中以{001...