生物可降解性聚碳酸亚丙酯／有机蒙脱土纳米复合材料的热氧老化

通过熔融插层法制备了聚碳酸亚丙酯（PPC）／有机蒙脱土（OMMT）纳米复合材料。研究了OMMT对PPC／OMMT纳米复合材料热氧老化的影响。结果表明，老化以后复合材料的拉伸强度以及断裂伸长率的保留率均高于纯PPC。加入OMMT后，复合材料的热老化性能明显改善。     

聚丙烯/蒙脱土复合材料的热氧老化性能

用3种蒙脱土(原土、OMMT1、OMMT2)与聚丙烯分别熔融插层复合.经X射线衍射(XRD)分析表明,3种蒙脱土均与聚丙烯成功插层复合,制备出聚丙烯/蒙脱土纳米复合材料.重点研究聚丙烯/蒙脱土纳米复合材料的热氧老化性能.结果表明,在聚丙烯材料中,添加少量蒙脱土不但可以提高材料的力学性能,而且明显改善材料的抗热氧老化性能.对3种PP/MMT复合材料热氧老化样品进行傅立叶红外(FTIR)分析和表面形貌观察,发现蒙脱土片层在聚丙烯中插层复合越充分(乃至剥离),其抗热氧老化效果就越明显.     

阻燃聚丙烯/蒙脱土纳米复合材料的燃烧性能

采用X射线衍射和透射电镜对所制备的聚丙烯/蒙脱土（PP/MMT）插层纳米复合材料的结构进行表征;通过热分析、锥形量热、氧指数、垂直燃烧测试对其热解和燃烧性能进行了研究.热分析表明蒙脱土片层在热解过程中显示出能量阻隔作用,提高了材料的热稳定性和成炭量;蒙脱土片层与膨胀型阻燃剂之间的协效作用使得纳米复合材料热释放速率、CO与CO2释放量及比消光面积明显降低;将不同阻燃级别的材料制成电视机壳进行全尺寸锥形量热仪实验表明,V-0级别的阻燃聚丙烯材料的火灾危险性最小.     

原位插层聚合法制备甲基苯基硅树脂/蒙脱土纳米复合材料

以甲基苯基二氯硅烷和甲基三氯硅烷为单体,采用原位插层聚合法制备甲基苯基硅树脂/有机蒙脱土(organic montmorillonite,OMMT)纳米复合材料,并通过红外光谱仪(FTIR)、X射线衍射仪(XRD)、透射电镜(TEM)和综合热分析仪(DSC)研究了复合材料的结构,探讨了超声波对蒙脱土分散性和复合材料热性能的影响.结果表明:制备的OMMT复合材料为含有端羟基的甲基苯基硅树脂复合材料;采用机械搅拌即可制备剥离型纳米复合材料,超声波辅助可进一步促进蒙脱土片层的分散,使片层剥离程度增加;OMMT的添加会降低有机硅树脂的热稳定性,且随着OMMT含量的增加,纳米复合材料的热失重先减小后增大,当OMMT质量分数为6%时复合材料的热稳定性最好,超声波辅助可进一步改善复合材料的耐热性能.     

生物可降解性聚碳酸亚丙酯/有机蒙脱土纳米复合材料的热氧老化

通过熔融插层法制备了聚碳酸亚丙酯(PPC)/有机蒙脱土(OMMT)纳米复合材料。研究了OMMT对PPC/OM-MT纳米复合材料热氧老化的影响。结果表明,老化以后复合材料的拉伸强度以及断裂伸长率的保留率均高于纯PPC。加入OMMT后,复合材料的热老化性能明显改善。     

聚碳酸亚丙酯／有机蒙脱土纳米复合材料的制备与性能

通过熔融插层法制备了聚碳酸亚丙酯（PPC）／有机蒙脱土（OMMT）复合材料。XRD分析表明：PPC／OMMT复合材料形成了插层型纳米复合结构。相对于纯PPC材料，纳米复合材料的拉伸性能和抗冲击性能得到了显著提高，但复合材料的断裂伸长率降低。当OMMT含量为6％时，PPC／OMMT纳米复合材料具有最优的力学性能和最高的玻璃化温度。     

聚碳酸亚丙酯/有机蒙脱土纳米复合材料的制备与性能

通过熔融插层法制备了聚碳酸亚丙酯(PPC)/有机蒙脱土(OMMT)复合材料。XRD分析表明:PPC/OMMT复合材料形成了插层型纳米复合结构。相对于纯PPC材料,纳米复合材料的拉伸性能和抗冲击性能得到了显著提高,但复合材料的断裂伸长率降低。当OMMT含量为6%时,PPC/OMMT纳米复合材料具有最优的力学性能和最高的玻璃化温度。     

丁腈橡胶/聚氯乙烯/改性蒙脱土纳米复合材料的结构与性能

采用胶乳共沉法和直接共混法制备了丁腈橡胶/聚氯乙稀/有机蒙脱土(NBR/PVC/OMMT)纳米复合材料.通过X射线衍射和透射电子显微镜对NBR/PVC/OMMT纳米复合材料的结构进行了表征,并研究其力学性能、耐油性能、耐热老化性能、硫化特性和动态力学性能.结果表明,所获得的复合材料是插层纳米复合材料;有机蒙脱土能够明显地促进NBR的硫化反应,使焦烧时间和硫化时间明显缩短;胶乳共沉法制备的纳米复合材料中的蒙脱土的分散更为均匀,其力学性能、耐油性能和耐老化性能明显优于直接共混法.     

有机插层剂对纳米复合材料介电性能的影响

采用熔融共混的方法分别制备了经两种有机插层剂(十八烷基季铵盐和双十八烷基苄基季铵盐)处理的交联聚乙烯/蒙脱土(XLPE/OMMT)纳米复合材料.不同插层剂处理的XLPE/OMMT纳米复合材料,介电谱表现出明显不同的特征:添加十八烷基季铵盐处理的蒙脱土,损耗峰为单峰;而添加双十八烷基苄基季铵盐处理的蒙脱土,损耗峰出现双峰.这与不同插层剂对蒙脱土在聚合物中的分散和插层效果有关.     

聚丙烯/有机改性蒙脱土纳米复合材料的制备及力学性能研究

针对两种有机蒙脱土(TJ-2型和KH-V6型),采用熔体插层法在双螺杆挤出机中制备出PP/OMMT纳米复合材料,并运用XRD和FTIR对所制得的复合材料进行表征.研究结果表明,两种OMMT片层都在PP基体中达到纳米级的分散.力学性能研究表明,相对PP而言,两种PP/OMMT纳米复合材料的硬度分别提高了11%和19%,抗冲击性能分别提高了18%和20%,且随着蒙脱土添加量的增加,冲击性能的变化符合逾渗脆韧转变机制.     

SBS/蒙脱土纳米复合材料插层结构影响因素和力学性能

为提高苯乙烯-丁二烯共聚物(SBS)的性能,采用溶液混合方法制备了SBS/有机蒙脱土(OMMT)纳米复合材料(NC).对影响NC插层结构的因素:混合条件、OMMT种类和含量、线型和星型结构SBS等进行了研究.XRD测试结果表明:存在一最佳混合时间和最佳OMMT含量;SBS在不同种类OMMT中插层效果明显不同,星型SBS更容易插层,制备的NC具有插层型结构.力学性能研究表明,添加OMMT对于所有复合材料均产生增强效果,其中以SBS4303/OMMT-DK1B NC最为明显,拉伸强度提高1倍多,并且断裂伸长率显著增加.表明OMMT具有增强和提高SBS弹性的双重作用.应力-应变曲线、300%定伸强度均从不同角度证实了OMMT的增强效果,但SBS/OMMT NC永久变形增大.     

一种无卤阻燃乙烯-醋酸乙烯酯共聚物的热分解动力学研究

通过极限氧指数法(LOI)和垂直燃烧(UL-94)测试考察了一种无卤阻燃乙烯-醋酸乙烯酯共聚物(EVA)的阻燃性能;利用热重分析法(TG)研究了纯EVA及阻燃EVA在不同升温速率下的热稳定性及热分解动力学,并采用Kissinger及Flynn-Wall-Ozawa方法计算了纯EVA和阻燃EVA的热分解表观活化能。结果表明,添加40%复合膨胀阻燃剂的EVA复合材料,极限氧指数达到28.6%,UL-94测试达到V-0级,残炭量相对纯EVA明显提高;随着升温速率增大,EVA和阻燃EVA的起始失重温度和各阶段的失重峰温均向高温方向移动;二者在第一阶段的热分解活化能均低于第二阶段,阻燃剂的添加使EVA的最大失重速率明显降低,热分解表观活化能提高,增强了材料的热稳定性和阻燃性。     

Amino-functionalized carbon nanotubes/polyphosphazene hybrids for improving the fire safety and mechanical properties of epoxy

To expand further modern industrial applications of epoxy resin (EP), the urgent problems of flammability and poor mechanical properties have to be solved. Therefore, amino-functionalized carbon nanotubes (AFP@CNTs) was designed and successfully synthesized to enhance the comprehensive properties, including fire safety and mechanical properties. Especially, the flame retardant mechanism, the combustion and pyrolysis process of EP/AFP@CNTs were investigated as well. With the addition of 1.5 ?wt% AFP@CNTs, the peak heat release rate (PHRR) and total heat release (THR) of EP were reduced by 27.6% and 29.0%, respectively, which may due to the cooperative effect between the phosphorus-nitrogen synergistic flame retardant of polyphosphazene and the cohesive phase flame retardant of carbon nanotubes. In addition, the mechanical performance of EP/AFP@CNTs composites were also investigated. The results showed that the impact strength, tensile strength and the storage modulus effectively increased by 65.0%, 29.0% and 13.2%, respectively. Meanwhile, the change of the combustion and pyrolysis process of EP/AFP@CNTs may be attributed to the catalytic effect of the amino-functionalized polyphosphazene, which could participate in the formation of epoxy thermal curing crosslinking network and catalyze the degradation process of epoxy resin.     

TDI-PTMG型PU/PMMA/OMMT纳米复合材料的结构及性能研究

将插层纳米复合技术与同步互穿聚合物网络(IPN)技术相结合,制备了聚氨酯(PU)/聚甲基丙烯酸甲酯(PMMA)/有机蒙脱土(OMMT)纳米复合材料.用透射电子显微镜(TEM)和力学性能测试研究了该复合材料和相应的PU/PMMA-IPN和PU材料的结构和力学性能.结果表明.PU/PMMA/OMMT纳米复合材料形成了插层/剥离型结构,其力学性能最优.对材料的制备工艺进行了研究,获得优化制备条件是:PU/PMMA质量比为60/40;OMMT,BPO,EGDMA添加量分别为单体MMA质量的5%,0.8%,2.0%,MOCA系数为0.9.     

新型阻燃三元乙丙橡胶的制备及其阻燃性能研究

采用微胶囊化聚磷酸铵与季戊四醇复配(APP∶PER=3∶1)填充三元乙丙橡胶(EPDM),制备新型阻燃EPDM材料,考察膨胀型阻燃剂(IFR)的填充量对EPDM材料的燃烧性能和热学性能的影响。结果表明,APP和PER复配使用,可协同提高EPDM的阻燃性能。当IFR填充量为40%时,材料的极限氧指数(LOI)可达到31%,UL94垂直燃烧等级达到V0级;最大热释放速率下降81.2%,总释放热降低30.4%;同时EPDM材料高温区热稳定性明显提高,且材料燃烧后可形成膨胀炭层,700℃下残渣量从0.9%提高至17.0%。     

蒙脱土对木质素基环氧树脂材料的影响

以碱木质素为原料,三氟化硼乙醚为催化剂,用环氧丙烷对碱木质素进行丙氧基化改性后,与环氧氯丙烷反应合成木质素基环氧树脂。以合成的木质素基环氧树脂为基体,有机化蒙脱土为增强材料,采用插层复合法制备了木质素基复合材料。木质素基环氧树脂与有机蒙脱土有很好的相容性,用T31和甲基六氢苯酐作固化剂时,木质素基环氧树脂/有机化蒙脱土(OMMT)复合材料的拉伸强度和冲击强度均高于未加蒙脱土的木质素基环氧树脂。极少量的有机蒙脱土的加入可同时提高木质素基环氧树脂的韧性和强度。     

P（MMA-MA）／OMMT纳米复合材料的制备及表征

通过原位乳液聚合法合成了聚(甲基丙烯酸甲酯-丙烯酸甲酯)(P(MMA-MA))/有机化蒙脱土(OMMT)纳米复合材料.使用X射线衍射仪(XRD)和透射电镜(TEM)表征了OMMT在P(MMA-MA)/OMMT纳米复合材料中的分散状况;用热失重分析仪(TGA)研究了材料的热稳定性;用裂解色谱-质谱联用仪(PGC-MS)分析了聚甲基丙烯酸甲酯(PMMA),聚丙烯酸甲酯(PMA)及P(MMA-MA)热降解机理.分析结果表明:P(MMA-MA)/OMMT纳米复合材料中已经形成了部分插层、部分剥离的结构;P(MMA-MA)/OMMT纳米复合材料的热稳定性随着OMMT加入量的增加而提高,并且当OMMT质量分数为5%时,其耐热性最好.另外,第二单体丙烯酸甲酯(MA)的加入也会增加P(MMA-MA)/OMMT的热稳定性.当甲基丙烯酸甲酯(MMA)与MA的质量比为40∶20时,在失重率为10%的热分解温度比PMMA/OMMT纳米复合材料的高25.3K.     

新型无卤阻燃聚丙烯的制备以及性能研究

将多聚磷酸铵（APP）、季戊四醇（PER）、三聚氰胺（MEL）及有机化蒙脱土（OMMT）于160oC下预混，制备了新型膨胀型阻燃剂（IFR）.以聚丙烯（PP）为基材，IFR为阻燃剂，聚苯乙烯-丁二烯-苯乙烯（SBS）为增韧剂，马来酸酐接枝聚丙烯（PP-g－MAH）为增容剂，通过熔融挤出制备了新型阻燃PP（FRPP）.通过LOI、TGA、XRD、SEM对材料的阻燃性、热稳定性、结晶性、冲击断面形貌进行了分析，并对材料的力学性能进行了测试.结果表明:加入IFR后，PP的极限氧指数由17升为28.5，起始分解温度由纯PP的440.8℃升高到455.3℃，600℃的成炭率提高15.26％；IFR诱导PP形成一定量晶型；少量OMMT在基体中以剥离形式存在，使晶粒尺寸得到细化，同时起到协同阻燃和增容作用，使材料在保持拉伸强度基本不变的情况下，缺口冲击强度提高1.92倍，冲击断面表现为韧性断裂.