提出了用粉末冶金法制备铜-锰固溶体的方法,研究了铜-锰粉末压坏的烧结特性,结果表明,利用粉末冶金法烧结铜-锰混合粉末,可以形成单相固溶体,其扩散机理属于单向扩散,即锰进入了铜,随着烧结温度的提高和保温时间的延长,铜-锰烧结压坏的密度和硬度都有下降的趋势,铜-锰粉末经混料,预压、热压成型后,按不同烧结参数（包括烧结温度和保温时间）在800℃烧结,保温50h,可制得铜-锰固溶体。     

TiH2粉末制备钛合金的烧结脱氢规律及工艺

 以TiH₂粉末为原料,通过压制成型和烧结工艺制备粉末钛合金,不同于传统钛粉末冶金方法。通过热分析和热膨胀技术研究不同球磨粒度TiH₂粉末的脱氢和收缩规律,以此入手研究了TiH₂粉末压坯和TiH₂-Al-V粉末压坯的烧结致密特性,以及影响烧结过程的主要工艺因素,包括烧结温度、烧结时间、升温速率、压坯密度、压坯成型方式、合金体系,并对烧结组织进行了分析。结果表明,TiH₂粉末球磨后脱氢温度降低,粉末越细,开始温度越低。TiH₂粉末压坯在烧结过程中脱氢后获得新鲜钛,其易发生黏接并引起α-Ti的强烈收缩,这时烧结体很容易致密,并获得相对密度大于99%坯体;相比之下,TiH₂-Al-V粉末压坯烧结时因为合金元素的溶解,不如纯TiH₂粉末压坯的烧结容易致密。TiH₂-Al-V粉末经过成型、烧结脱氢可获得典型的层片状α+β钛合金组织,合金元素分布均匀。     

用粉末冶金法制备锰铋合金的研究

研究了用粉末冶金法制备锰铋合金时,烧结温度、保温时间、化学成分以及原料中锰粉的粗细和氧化程度对样品磁性的影响。用MnBi相形成时的反应——包晶反应的特点,对所得结果给予了解释。     

3%C-Cu机械球磨复合粉末的烧结

为了给后续的致密化工序(如热挤压)提供较高质量的烧结坯,用扫描电镜和光学显微镜分析了3%C-Cu机械球磨复合粉末所制备烧结坯的显微组织,并研究了工艺参数对其相对致密度的影响规律.结果表明,烧结温度对未机械球磨混合粉烧结行为的影响很大,而机械球磨复合粉对烧结温度不敏感.真空热压烧结可以明显地促进致密化过程.提高烧结温度、延长烧结保温时间或增加热压压强,均有助于提高烧结坯的相对致密度.在相同条件下,烧结坯的相对致密度随着复合粉末机械球磨时间的延长而降低.     

铜-铝系合金粉末压坯烧结机理

针对铜-铝系粉末压坯烧结出现的异常膨胀,采用熔铸中间合金γ_2(Cu_9Al_4)相实现 Al合金化,Cu-γ_2 预合金化处理,及添加羰基镍实现微量液相烧结等措施。解决了由于克肯达尔效应、相体积效应及相变潜热等综合作用引起的异常膨胀。为开发铜-铝系粉末冶金产品奠定了理论及实践基础。     

Ti-47．5Al-2．5V-1．0Cr注射成形

以Ti-47.5Al-2.5V-1.0Cr(原子分数,%)气雾化预合金粉末为原料,采用粉末注射成形工艺制备了TiAl合金材料,研究了该TiAl合金脱脂工艺对脱脂坯碳氧残留量和组织的影响规律及烧结工艺对烧结体显微组织、密度和压缩性能的影响规律. 结果表明:在脱脂温度600℃、保温时间为1h和真空脱脂气氛条件下脱除坯体中剩余粘结剂,坯体中残余碳氧含量(质量分数)分别为0.059%和0.12%;脱脂温度从600℃升到1000℃,粉末由枝状组织转变为近γ组织;烧结温度在1410～1450℃,保温时间在1h以内,烧结体可以快速致密化;在1450℃保温30min,烧结体相对密度可以达到95%,烧结体的抗压强度为2105MPa,压缩率达到30.9%,接近铸态合金力学性能;随烧结温度升高,烧结体中的γ相逐渐减少,组织由近片层组织逐渐转变为全片层组织.     

添加剂强化Fe-Si粉末压坯合金化和烧结过程机理的探讨(英文)

本文研究了碳酸化合物对Fe-Si混合粉末压坯合金化和烧结过程的影响。实验发现:添加少量的碳酸钾或碳酸钠可以显著地降低Fe-Si的合金化温度、强化合金化和烧结过程。作者认为:这种强化效果是由于碳酸化合物与SiO_2反应形成液态硅酸盐玻璃,从而去除了Si颗粒表面的氧化膜,使Fe-Si之间具有良好的接触;含有添加剂的粉末压坯所表现出的较大烧结收缩与Fe-Si体系中的单向扩散和液态玻璃相存在所产生的活化烧结有关。     

高速压制制备高密度纯铁软磁材料

以退火纯铁粉末为原料,采用粉末退火结合高速压制技术的方法制得高密度压坯(7.70 g·cm-3),经烧结后获得高密度高性能的纯铁软磁材料.研究退火粉末的高速压制行为,以及烧结时间和烧结温度对材料磁性能和晶粒大小的影响.结果显示：退火粉末的压坯密度随压制速度的增加而增加,压坯密度最高可达到7.70 g·cm-3,相对密度可达到98.10%.烧结温度为1450益,烧结时间为4 h时,材料密度达到7.85 g·cm-3,相对密度为99.96%,最大磁导率达到13.60 mH·m-1,饱和磁感应强度为1.87 T,矫顽力为56.50 A·m-1.     

镁颗粒在烧结过程中的变化方式及其对泡沫铝制备的影响

 研究了粉末冶金法制备泡沫铝材料过程中,提高可发泡预制坯致密度的方法.分析了预制坯制备过程中影响致密度的因素以及致密化过程;研究了烧结处理过程中烧结温度、烧结时间对预制坯内部组织结构及其致密度的影响.着重分析了烧结处理对Mg颗粒以及泡沫铝孔径结构的影响.对于粉末粒度为75~150μm的原料粉末来说,将在400MPa的压制压力下制备的预制坯进行450℃烧结处理2h以上,可提高预制坯的致密度并能够增加基体的连续性,烧结后Mg颗粒尺寸为原来的2~3倍.实验结果表明：采用冷压的方式,在400MPa的压力下,对经过450℃烧结2h后的预制坯进行发泡,可以得到孔径均匀、孔隙率高的泡沫铝材料.     

粉末铁基高温合金的制备工艺研究

采用粉末机械合金化-温压成型-真空烧结等方法制备了氧化物弥散强化铁基高温合金MA956,并对其制备工艺和组织性能进行了研究。结果表明,高能振动球磨4h粉末颗粒细小均匀,已经基本实现了合金化,将其在120℃、500MPa条件下进行温压成型,压坯密度比常温模压工艺提高了0．3g／cm3;烧结温度对烧结体组织和性能有较大的影响,粉末压坯在1350℃烧结其致密度最高,为90．8％,且显微组织致密性好。     

扩散温度对Cu－Sn粉末压制与烧结性能的影响

热扩散法是制取部分合金化Ｃｕ－Ｓｎ粉末的途径之一，作者研究了扩散温度对Ｃｕ－Ｓｎ粉末压制与烧结性能的影响，实验结果表明，Ｃｕ－Ｓｎ粉末的压实性及烧结胀大现象，都随着扩散温度的提高而降低，Ｃｕ粉颗粒越粗，获得具有相同烧结性能的Ｃｕ－Ｓｎ粉末的扩散温度越高。     

镍包覆铜复合粉末烧结体界面扩散行为研究

利用固相烧结法将镍包铜粉成功地制成了块状烧结体,通过SEM、XRD和EDS研究了烧结过程中镍包铜粉中界面的迁移情况.结果表明,随烧结温度升高,颗粒内原子扩散系数越大,烧结体界面迁移越容易,形成较大的晶粒,同时界面组织也比较均匀.在扩散过程中,由于镍的扩散系数比铜大,镍层扩散进入铜形成了铜镍固溶体,界面呈现单向迁移.     

微波加热与常规加热硅锰粉固相脱硅动力学比较

采用微波加热和常规加热对硅锰粉和巴西粉锰的脱硅反应进行了动力学行为研究,以巴西粉锰为脱硅剂,与硅锰粉中的硅发生氧化还原反应.微波加热和常规加热分别加热到不同温度并保温一定时间,测定产物中硅含量并计算固相脱硅反应的表观活化能.实验表明:单一和混合料均可在微波场中快速升温.随着温度的升高和保温时间的延长,两种加热方式脱硅率均随之提高,在相同实验条件下,微波加热的脱硅率和反应速率均高于常规加热,微波加热可以提高固相脱硅率;微波加热固相脱硅反应的限制性环节为扩散环节,其表观活化能为102.93 kJ·mol-1,常规加热脱硅反应的表观活化能为180 kJ·mol-1,说明微波加热能改善固相脱硅的动力学条件,提高固相脱硅反应速率,降低脱硅反应的活化能.     

Cu-Zn-Al2O3 nanocomposites: study of microstructure,corrosion, and wear properties

Alumina nanoparticles were added to a Cu-Zn alloy to investigate their effect on the microstructural, tribological, and corrosion properties of the prepared alloys. Alloying was performed using a mixture of copper and zinc powders with 0vol% and 5vol% of α-Al nanopowder in a satellite ball mill. The results showed that the Cu-Zn solid solution formed after 18 h of mechanical alloying. The mechan-ically alloyed powder was compacted followed by sintering of the obtained green compacts at 750℃ for 30 min. Alumina nanoparticles were uniformly distributed in the matrix of the Cu-Zn alloy. The tribological properties were evaluated by pin-on-disk wear tests, which revealed that, upon the addition of alumina nanoparticles, the coefficient of friction and the wear rate were reduced to 20% and 40%, respectively. The corrosion properties of the samples exposed to a 3.5wt% NaCl solution were studied using the immersion and potentiodynamic polarization methods, which revealed that the addition of alumina nanoparticles reduced the corrosion current of the nanocomposite by 90%.     

GdAlO粉体的溶胶凝胶法制备工艺及烧结行为研究

以Gd2O3、Al（NO3）3·9H2O和HNO3为原料，柠檬酸为络合剂，通过溶胶凝胶法制备前驱体，经过1000℃，保温2h热处理得到了纯相铝酸钆（GdAlO3）粉体。通过研究GdAlO3坯体样品的恒速无压烧结曲线发现，当升温速率为5℃／min时，样品在957℃开始收缩，烧结温度为1600℃时，最大收缩率为16．17％；通过计算得出GdAIO3坯体在烧结温度200-1000℃范围内平均线膨胀系数是9．38×10^-8／℃，以烧结曲线为基础，使用基于相对收缩率的Arrhenius关系，计算得到铝酸钆的烧结激活能为22．4kJ／mol，低于氧化铝的烧结激活能，说明其会促进氧化铝的烧结。     

Cu-Zn-Al2O3 nanocomposites:study of microstructure,corrosion,and wear properties

Alumina nanoparticles were added to a Cu-Zn alloy to investigate their effect on the microstructural, tribological, and corrosion properties of the prepared alloys. Alloying was performed using a mixture of copper and zinc powders with 0vol% and 5vol% of α-Al nanopowder in a satellite ball mill. The results showed that the Cu-Zn solid solution formed after 18 h of mechanical alloying. The mechanically alloyed powder was compacted followed by sintering of the obtained green compacts at 750℃ for 30 min. Alumina nanoparticles were uniformly distributed in the matrix of the Cu-Zn alloy. The tribological properties were evaluated by pin-on-disk wear tests, which revealed that, upon the addition of alumina nanoparticles, the coefficient of friction and the wear rate were reduced to 20% and 40%, respectively. The corrosion properties of the samples exposed to a 3.5wt% NaCl solution were studied using the immersion and potentiodynamic polarization methods, which revealed that the addition of alumina nanoparticles reduced the corrosion current of the nanocomposite by 90%.     

机械活化粉末制备W-Cu合金的微观组织

为了改善制备工艺和提高W-Cu合金的密度与性能,对原料粉末进行了机械活化处理,通过成形和烧结制备了W-Cu合金,考察了活化后粉末的变化,观察了合金的烧结组织并测量了密度.结果表明,机械活化能增大钨铜粉末的表面能和晶格畸变能,有效地促进烧结,改善烧结组织;烧结体中存在大量团絮状组织,团粒内部钨颗粒主要以固相方式烧结在一起,而团粒之间则以液相烧结为主.烧结组织细密、均匀,相对密度达98%以上;烧结组织中钨铜两相在微米尺度下仍然结合良好,部分界面出现了互溶.     

纳米陶瓷研究进展

综述纳米陶瓷的性能，粉体制备，烧结及结构研究现状，分析实现纳米陶瓷成功制备的关键因素。得出结论：在纳米陶瓷制备过程中，无团聚高致纱坯是前提，烧结过程中晶粒生长的抑制是关键。     

烧结温度对高速压制制备弥散强化铜材料导电率的影响

弥散强化铜材料具有高强度和高导电性的特性,孔洞是影响导电率的重要因素.本文采用高速压制成形技术,对Al2 O3质量分数为0.9%的弥散强化铜粉压制成形,研究了压制速度对生坯的影响.当压制速度为9.4 m·s-1时得到密度为8.46 g·cm-3的生坯.研究了烧结温度对烧结所得Al2 O3弥散强化铜试样导电率的影响.当生坯密度相同时,烧结温度越高,所得试样的导电率也越高.断口与金相分析表明：烧结温度为950℃时,烧结不充分,颗粒边界以及孔洞多而明显,孔洞形状不规则;烧结温度为1080℃时,颗粒边界消失,孔洞圆化,韧窝出现,烧结坯的电导率为71.3%IACS.     

悬浊液进样原子吸收法测定茶叶中铜和锰的研究

本文介绍了一种操作简单、省时的茶叶中铜、锰的快速分析方法.经烘干、粉碎后的茶叶样品在60%甘油——水体系中制成均匀的悬浊液,然后直接被引入石墨杯原子化器内,进行原子吸收测定.作者对用该法测定茶叶中的铜、锰的各种实验条件进行了充分研究,包括悬浊液体系的组成,茶叶样品颗粒大小的影响及石墨炉升温程序等.实验结果表明,该法除具有粉末直接进样原子吸收法的各种优点外,还保持了溶液进样法的精度高等许多特点.该法不仅可用于茶叶中金属元素的快速分析,同样还可用于其它样品中各种元素的测定.