Sintering behaviors and consolidation mechanism of high-chromium vanadium and titanium magnetite fines |
| |
| Affiliation: | School of Materials and Metal urgy, Northeastern University, Shenyang 110819, China |
| |
| Abstract: | To achieve high efficiency utilization of high-chromium vanadium–titanium magnetite (V–Ti–Cr) fines, an investigation of V–Ti–Cr fines was conducted using a sinter pot. The chemical composition, particle parameters, and granulation of V–Ti–Cr mixtures were analyzed, and the effects of sintering parameters on the sintering behaviors were investigated. The results indicated that the optimum quick-lime dosage, mixture moisture, wetting time, and granulation time for V–Ti–Cr fines are 5wt%, 7.5wt%, 10 min, and 5–8 min, respectively. Meanwhile, the vertical sintering speed, yield, tumbler strength, and productivity gains were shown to be 21.28 mm/min, 60.50wt%, 58.26wt%, and 1.36 t?m?2?h?1, respectively. Furthermore, the consolidation mechanism of V–Ti–Cr fines was clarified, revealing that the consolidation of a V–Ti–Cr sinter requires an approximately 14vol% calcium ferrite liquid-state, an approximately 15vol% silicate liq-uid-state, a solid-state reaction, and the recrystallization of magnetite. Compared to an ordinary sinter, calcium ferrite content in a V–Ti–Cr sinter is lower, while the perovskite content is higher, possibly resulting in unsatisfactory sinter outcomes. |
| |
| Keywords: | magnetite chromium vanadium titanium ore sintering consolidation mineralogy |
| 本文献已被 万方数据 等数据库收录！ |
| 点击此处可从《矿物冶金与材料学报》浏览原始摘要信息 |
|
点击此处可从《矿物冶金与材料学报》下载全文 |
|